Titanium Grade 2 vs Ti Grade 30
Titanium · grade comparison
Titanium Grade 2 and Ti Grade 30 are both titanium grades. Grade 2 is the stronger of the two: yield strength 380 MPa (55.1 ksi) against 330 MPa (47.9 ksi) for Ti Grade 30, about 15% more. Ti Grade 30 is harder — 160 HB against 150 HB for Grade 2 — which matters for wear surfaces and threads. On the shop floor, Ti Grade 30 sits in a lower cost tier (high, $$$$) than Grade 2 (specialty, $$$$$).
Grade 2Choose it when strength drives the design.
Ti Grade 30Choose it when surface hardness matters, or when cost is the deciding factor.
Grade 2 vs Ti Grade 30: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Yield Strength (0.2% offset)
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Shear Modulus 45 GPa6.5 Msi · Bulk Modulus 110 GPa16 Msi · Poisson's Ratio 0.34 · Tensile Strength (Ultimate) 440 MPa63.8 ksi · Elongation at Break 28% · Fracture Toughness (K_IC) 70 MPa·√m63.7 ksi·√in · Hardness, Rockwell B 80 HRB
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 4.51 g/cm³0.16 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Latent Heat of Fusion
Min Service Temperature
Same in both: Specific Heat Capacity 523 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 8.6 µm/m·K4.8 µin/in·°F · Max Service Temperature (continuous) 300°C572 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 3.1 % IACS · Electrical Resistivity 5.6×10⁻⁷ Ω·m22 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Stiffness (E / density)
Modulus of Resilience
Same in both: Specific Strength (UTS / density) 98 kN·m/kg · Thermal Diffusivity 7 mm²/s · Thermal Shock Resistance Index 8
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Grade 2 | Ti Grade 30 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$$ Specialty | $$$$ High |
| Min. machined wall | 1 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Anodizing Type II | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| TiAlN | Yes | — |
| TiB2 | Yes | — |
| TiCN | Yes | — |
| TiN | Yes | — |
| WC/C | Yes | — |
They share 1 finish: Plasma Spray.
Grade 2 vs Ti Grade 30 — frequently asked
Is Grade 2 stronger than Ti Grade 30?
Yes. Grade 2 has a typical yield strength of 380 MPa (55.1 ksi) against 330 MPa (47.9 ksi) for Ti Grade 30 — about 15% more. Tensile strength is 440 MPa (63.8 ksi) vs 440 MPa (63.8 ksi).
Which is cheaper, Grade 2 or Ti Grade 30?
Ti Grade 30 is the lower-cost material: it sits in the high tier ($$$$) while Grade 2 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, Grade 2 or Ti Grade 30?
Grade 2, by a small margin. Both rate fair for machinability — 40/100 against 35/100 for Ti Grade 30; for welding the order is Grade 2 first (excellent, 90/100) then Ti Grade 30 (excellent, 85/100).