Titanium Grade 2 and Grade 2H are both titanium grades. Grade 2 is the stronger of the two: yield strength 380 MPa (55.1 ksi) against 350 MPa (50.8 ksi) for Grade 2H, about 9% more. Grade 2 is the more ductile: elongation 28% versus 25% for Grade 2H, and Grade 2H is harder (160 HB vs 150 HB). On the shop floor, Grade 2H sits in a lower cost tier (high, $$$$) than Grade 2 (specialty, $$$$$).
Grade 2Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
Grade 2HChoose it when cost is the deciding factor.
Grade 2 vs Grade 2H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 45 GPa6.5 Msi · Bulk Modulus 110 GPa16 Msi · Poisson's Ratio 0.34 · Shear Strength 320 MPa46.4 ksi · Fracture Toughness (K_IC) 70 MPa·√m63.7 ksi·√in · Charpy V-Notch Impact (RT) 40 J29.5 ft·lbf
Physical
Density and transition temperatures.
Same in both: Density 4.51 g/cm³0.16 lb/in³ · Melting Point (Solidus) 1,665°C3,029 °F · Liquidus Temperature 1,670°C3,038 °F
Thermal
How each material carries heat and how hot it can run.
Latent Heat of Fusion
Same in both: Thermal Conductivity 16.4 W/m·K9.5 BTU/hr·ft·°F · Specific Heat Capacity 523 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 8.6 µm/m·K4.8 µin/in·°F · Max Service Temperature (continuous) 300°C572 °F · Min Service Temperature -250°C-418 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 3.1 % IACS · Electrical Resistivity 5.6×10⁻⁷ Ω·m22 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Weldability
Castability
Brazeability / Solderability
Polishability
Same in both: Machinability 40 / 100 · Formability (cold) 78 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 25%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Same in both: Thermal Diffusivity 7 mm²/s · Thermal Shock Resistance Index 8
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Grade 2 | Grade 2H |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$$ Specialty | $$$$ High |
| Min. machined wall | 1 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Anodizing Type II | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| TiAlN | Yes | — |
| TiB2 | Yes | — |
| TiCN | Yes | — |
| TiN | Yes | — |
| WC/C | Yes | — |
They share 1 finish: Plasma Spray.
Grade 2 vs Grade 2H — frequently asked
Is Grade 2 stronger than Grade 2H?
Yes. Grade 2 has a typical yield strength of 380 MPa (55.1 ksi) against 350 MPa (50.8 ksi) for Grade 2H — about 9% more. Tensile strength is 440 MPa (63.8 ksi) vs 460 MPa (66.7 ksi).
Which is cheaper, Grade 2 or Grade 2H?
Grade 2H is the lower-cost material: it sits in the high tier ($$$$) while Grade 2 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, Grade 2 or Grade 2H?
Grade 2. Its weldability rates excellent (90/100) against excellent (85/100) for Grade 2H.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Grade 2 and Grade 2H side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.