Titanium ERTi-2 vs ERTi-7
Titanium · grade comparison
Titanium ERTi-2 and ERTi-7 are both titanium grades. ERTi-2 is the stronger of the two: yield strength 380 MPa (55.1 ksi) against 330 MPa (47.9 ksi) for ERTi-7, about 15% more; tensile strength follows at 480 MPa (69.6 ksi) vs 420 MPa (60.9 ksi).
ERTi-2Choose it when strength drives the design.
ERTi-2 vs ERTi-7: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Vickers
Same in both: Shear Modulus 45 GPa6.5 Msi · Bulk Modulus 110 GPa16 Msi · Poisson's Ratio 0.34 · Reduction in Area 45% · Charpy V-Notch Impact (RT) 45 J33.2 ft·lbf · Hardness, Brinell 155 HB · Hardness, Rockwell B 80 HRB
Physical
Density and transition temperatures.
Same in both: Density 4.51 g/cm³0.16 lb/in³ · Melting Point (Solidus) 1,660°C3,020 °F · Liquidus Temperature 1,670°C3,038 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 16.4 W/m·K9.5 BTU/hr·ft·°F · Specific Heat Capacity 523 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 8.6 µm/m·K4.8 µin/in·°F · Latent Heat of Fusion 325 J/g140 BTU/lb · Max Service Temperature (continuous) 315°C599 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 3.1 % IACS · Electrical Resistivity 5.6×10⁻⁷ Ω·m22 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Machinability 40 / 100 · Brazeability / Solderability 45 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Shock Resistance Index
Same in both: Thermal Diffusivity 7 mm²/s
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | ERTi-2 | ERTi-7 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 1 finish: Plasma Spray.
ERTi-2 vs ERTi-7 — frequently asked
Is ERTi-2 stronger than ERTi-7?
Yes. ERTi-2 has a typical yield strength of 380 MPa (55.1 ksi) against 330 MPa (47.9 ksi) for ERTi-7 — about 15% more. Tensile strength is 480 MPa (69.6 ksi) vs 420 MPa (60.9 ksi).
Which is cheaper, ERTi-2 or ERTi-7?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose ERTi-2 over ERTi-7?
Pick ERTi-2 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in ERTi-2 and ERTi-7 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.