Steel X16CrMo5-1 +A vs X16CrMo5-1 +N
Steel · X16CrMo5-1 temper comparison
X16CrMo5-1 +A and X16CrMo5-1 +N are two conditions of the same steel grade, X16CrMo5-1: +A (annealed) versus +N (normalized). The chemistry is identical, so every difference below comes from the condition. X16CrMo5-1 +N is the stronger of the two: yield strength 650 MPa (94.3 ksi) against 330 MPa (47.9 ksi) for X16CrMo5-1 +A, about 97% more; tensile strength follows at 900 MPa (131 ksi) vs 560 MPa (81.2 ksi). In exchange, X16CrMo5-1 +A is the more ductile: elongation 24% versus 14% for X16CrMo5-1 +N, and X16CrMo5-1 +N is harder (280 HB vs 170 HB). X16CrMo5-1 +N runs hotter in service (600°C vs 550°C continuous). On the shop floor, X16CrMo5-1 +A machines more easily (fair vs poor) and X16CrMo5-1 +A welds better (50 vs 35 out of 100).
X16CrMo5-1 +AChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
X16CrMo5-1 +NChoose it when strength drives the design, or when the part sees heat.
X16CrMo5-1 +A vs X16CrMo5-1 +N: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 213 GPa30.9 Msi · Shear Modulus 82 GPa11.9 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3 · Fracture Toughness (K_IC) 90 MPa·√m81.9 ksi·√in
Physical
Density and transition temperatures.
Same in both: Density 7.75 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,450°C2,642 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 36 W/m·K20.8 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.3 µm/m·K6.3 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.9 % IACS · Electrical Resistivity 6×10⁻⁷ Ω·m23.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.58 V · Corrosion Resistance 26 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 40 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 34 MJ/kg14,617 BTU/lb · Embodied Carbon (primary production) 2.4 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
X16CrMo5-1 +A vs X16CrMo5-1 +N — frequently asked
Is X16CrMo5-1 +N stronger than X16CrMo5-1 +A?
Yes. X16CrMo5-1 +N has a typical yield strength of 650 MPa (94.3 ksi) against 330 MPa (47.9 ksi) for X16CrMo5-1 +A — about 97% more. Tensile strength is 900 MPa (131 ksi) vs 560 MPa (81.2 ksi).
Which condition does FabDigit quote by default, +A or +N?
+NT is the default X16CrMo5-1 condition in the FabDigit quote flow (neither +A nor +N). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, X16CrMo5-1 +A or X16CrMo5-1 +N?
X16CrMo5-1 +A. Its machinability rates fair (52/100) against poor (30/100) for X16CrMo5-1 +N; for welding the order is X16CrMo5-1 +A first (fair, 50/100) then X16CrMo5-1 +N (fair, 35/100).