Steel SUP13-CD vs SUP13-N
Steel · SUP13 temper comparison
SUP13-CD and SUP13-N are two conditions of the same steel grade, SUP13: CD (cold drawn) versus N (normalized). The chemistry is identical, so every difference below comes from the condition. SUP13-CD is the stronger of the two: yield strength 900 MPa (131 ksi) against 600 MPa (87 ksi) for SUP13-N, about 50% more; tensile strength follows at 1,050 MPa (152 ksi) vs 960 MPa (139 ksi). In exchange, SUP13-N is the more ductile: elongation 14% versus 8% for SUP13-CD, and SUP13-CD is harder (310 HB vs 285 HB). SUP13-N runs hotter in service (300°C vs 200°C continuous).
SUP13-CDChoose it when strength drives the design.
SUP13-NChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
SUP13-CD vs SUP13-N: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 206 GPa29.9 Msi · Shear Modulus 79.5 GPa11.5 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Fatigue Strength (Endurance Limit) 430 MPa62.4 ksi
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.5 µm/m·K6.9 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 35 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 30 MJ/kg12,898 BTU/lb · Embodied Carbon (primary production) 2.1 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
SUP13-CD vs SUP13-N — frequently asked
Is SUP13-CD stronger than SUP13-N?
Yes. SUP13-CD has a typical yield strength of 900 MPa (131 ksi) against 600 MPa (87 ksi) for SUP13-N — about 50% more. Tensile strength is 1,050 MPa (152 ksi) vs 960 MPa (139 ksi).
Which condition does FabDigit quote by default, CD or N?
QT 44-48 HRC is the default SUP13 condition in the FabDigit quote flow (neither CD nor N). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose SUP13-CD over SUP13-N?
Pick SUP13-CD when strength drives the design. Pick SUP13-N when the part is bent, formed or impact-loaded, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in SUP13-CD and SUP13-N side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.