Steel G34CrMo4 +A vs G34CrMo4 +QT1
Steel · G34CrMo4 temper comparison
G34CrMo4 +A and G34CrMo4 +QT1 are two conditions of the same steel grade, G34CrMo4: +A (annealed) versus +QT1 (quenched and tempered, lower strength class). The chemistry is identical, so every difference below comes from the condition. G34CrMo4 +QT1 is the stronger of the two: yield strength 570 MPa (82.7 ksi) against 360 MPa (52.2 ksi) for G34CrMo4 +A, about 58% more; tensile strength follows at 760 MPa (110 ksi) vs 620 MPa (89.9 ksi). In exchange, G34CrMo4 +A is the more ductile: elongation 19% versus 14% for G34CrMo4 +QT1, and G34CrMo4 +QT1 is harder (235 HB vs 185 HB). On the shop floor, G34CrMo4 +A machines more easily (good vs fair).
G34CrMo4 +AChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
G34CrMo4 +QT1Choose it when strength drives the design.
G34CrMo4 +A vs G34CrMo4 +QT1: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 580 MPa84.1 ksi · Shear Strength 460 MPa66.7 ksi · Fracture Toughness (K_IC) 75 MPa·√m68.3 ksi·√in · Hardness, Rockwell C 22 HRC
Physical
Density and transition temperatures.
Same in both: Density 7.83 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 42 W/m·K24.3 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.3 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 7.8 % IACS · Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Same in both: Formability (cold) 10 / 100 · Castability 65 / 100 · Brazeability / Solderability 45 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 26 MJ/kg11,178 BTU/lb · Embodied Carbon (primary production) 2.1 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 75%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
G34CrMo4 +A vs G34CrMo4 +QT1 — frequently asked
Is G34CrMo4 +QT1 stronger than G34CrMo4 +A?
Yes. G34CrMo4 +QT1 has a typical yield strength of 570 MPa (82.7 ksi) against 360 MPa (52.2 ksi) for G34CrMo4 +A — about 58% more. Tensile strength is 760 MPa (110 ksi) vs 620 MPa (89.9 ksi).
Which condition does FabDigit quote by default, +A or +QT1?
+QT1 is the default G34CrMo4 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, G34CrMo4 +A or G34CrMo4 +QT1?
G34CrMo4 +A. Its machinability rates good (62/100) against fair (50/100) for G34CrMo4 +QT1; for welding the order is G34CrMo4 +A first (fair, 45/100) then G34CrMo4 +QT1 (fair, 40/100).