Steel A387 Gr 21 vs AR400
Steel · grade comparison
Steel A387 Gr 21 and AR400 are both steel grades. AR400 is the stronger of the two: yield strength 1,050 MPa (152 ksi) against 380 MPa (55.1 ksi) for A387 Gr 21, about 176% more; tensile strength follows at 1,250 MPa (181 ksi) vs 560 MPa (81.2 ksi). In exchange, A387 Gr 21 is the more ductile: elongation 22% versus 11% for AR400, and AR400 is harder (400 HB vs 170 HB). A387 Gr 21 runs hotter in service (550°C vs 250°C continuous) and AR400 conducts heat better (42 W/m·K vs 34 W/m·K). On the shop floor, A387 Gr 21 machines more easily (good vs poor), AR400 welds better (good vs fair), and A387 Gr 21 sits in a lower cost tier (standard, $$) than AR400 (premium, $$$).
A387 Gr 21Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
AR400Choose it when strength drives the design, or when it will be welded.
A387 Gr 21 vs AR400: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Hardness, Rockwell C
Same in both: Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Same in both: Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 25%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | A387 Gr 21 | AR400 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | — | Q&T |
| Relative cost | $$ Standard | $$$ Premium |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| E-Coating | — | Yes |
| HVOF Coating | — | Yes |
| Hot-Dip Galvanizing | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
A387 Gr 21 vs AR400 — frequently asked
Is AR400 stronger than A387 Gr 21?
Yes. AR400 has a typical yield strength of 1,050 MPa (152 ksi) against 380 MPa (55.1 ksi) for A387 Gr 21 — about 176% more. Tensile strength is 1,250 MPa (181 ksi) vs 560 MPa (81.2 ksi).
Which is cheaper, A387 Gr 21 or AR400?
A387 Gr 21 is the lower-cost material: it sits in the standard tier ($$) while AR400 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, A387 Gr 21 or AR400?
A387 Gr 21. Its machinability rates good (55/100) against poor (22/100) for AR400; for welding the order is AR400 first (good, 55/100) then A387 Gr 21 (fair, 45/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in A387 Gr 21 and AR400 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.