Steel A216 WCA vs GP280GH
Steel · grade comparison
Steel A216 WCA and GP280GH are both steel grades. GP280GH is the stronger of the two: yield strength 310 MPa (45 ksi) against 255 MPa (37 ksi) for A216 WCA, about 22% more; tensile strength follows at 540 MPa (78.3 ksi) vs 455 MPa (66 ksi). In exchange, A216 WCA is the more ductile: elongation 31% versus 24% for GP280GH, and GP280GH is harder (165 HB vs 130 HB).
A216 WCAChoose it when the part is bent, formed or impact-loaded.
GP280GHChoose it when strength drives the design.
A216 WCA vs GP280GH: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Density
Same in both: Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Min Service Temperature
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Max Service Temperature (continuous) 425°C797 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 10 % IACS · Electrical Resistivity 1.7×10⁻⁷ Ω·m6.69 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Castability
Polishability
Same in both: Formability (cold) 20 / 100 · Brazeability / Solderability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 10
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | A216 WCA | GP280GH |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$ Standard | $$ Standard |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
A216 WCA vs GP280GH — frequently asked
Is GP280GH stronger than A216 WCA?
Yes. GP280GH has a typical yield strength of 310 MPa (45 ksi) against 255 MPa (37 ksi) for A216 WCA — about 22% more. Tensile strength is 540 MPa (78.3 ksi) vs 455 MPa (66 ksi).
Which is cheaper, A216 WCA or GP280GH?
Both sit in the same relative cost tier ($$, standard); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, A216 WCA or GP280GH?
A216 WCA, by a small margin. Both rate good for machinability — 68/100 against 60/100 for GP280GH; for welding the order is A216 WCA first (excellent, 85/100) then GP280GH (very good, 78/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in A216 WCA and GP280GH side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.