Steel 55Cr3 vs P355ML2
Steel · grade comparison
Steel 55Cr3 and P355ML2 are both steel grades. 55Cr3 is the stronger of the two: yield strength 480 MPa (69.6 ksi) against 390 MPa (56.6 ksi) for P355ML2, about 23% more; tensile strength follows at 800 MPa (116 ksi) vs 520 MPa (75.4 ksi). In exchange, P355ML2 is the more ductile: elongation 26% versus 16% for 55Cr3, and 55Cr3 is harder (225 HB vs 155 HB). P355ML2 conducts electricity better (9 % IACS vs 7.8 % IACS). On the shop floor, P355ML2 machines more easily (good vs fair), P355ML2 welds better (excellent vs poor), and P355ML2 sits in a lower cost tier (budget, $) than 55Cr3 (standard, $$).
55Cr3Choose it when strength drives the design.
P355ML2Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
55Cr3 vs P355ML2: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Rockwell C
Hardness, Vickers
Same in both: Bulk Modulus 160 GPa23.2 Msi
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Min Service Temperature
Same in both: Max Service Temperature (continuous) 400°C752 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Galvanic Potential (seawater, vs SCE)
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Same in both: Machinability Rating (AISI 1212 = 100 %) 55%
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 45 L/kg5.4 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 55Cr3 | P355ML2 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | Annealed | — |
| Relative cost | $$ Standard | $ Budget |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| HVOF Coating | Yes | — |
| Hot-Dip Galvanizing | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
55Cr3 vs P355ML2 — frequently asked
Is 55Cr3 stronger than P355ML2?
Yes. 55Cr3 has a typical yield strength of 480 MPa (69.6 ksi) against 390 MPa (56.6 ksi) for P355ML2 — about 23% more. Tensile strength is 800 MPa (116 ksi) vs 520 MPa (75.4 ksi).
Which is cheaper, 55Cr3 or P355ML2?
P355ML2 is the lower-cost material: it sits in the budget tier ($) while 55Cr3 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 55Cr3 or P355ML2?
P355ML2. Its machinability rates good (60/100) against fair (50/100) for 55Cr3; for welding the order is P355ML2 first (excellent, 92/100) then 55Cr3 (poor, 25/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 55Cr3 and P355ML2 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.