Steel 35# vs G10MnMoV6-3
Steel · grade comparison
Steel 35# and G10MnMoV6-3 are both steel grades. G10MnMoV6-3 is the stronger of the two: yield strength 540 MPa (78.3 ksi) against 330 MPa (47.9 ksi) for 35#, about 64% more; tensile strength follows at 690 MPa (100 ksi) vs 560 MPa (81.2 ksi). In exchange, 35# is the more ductile: elongation 22% versus 18% for G10MnMoV6-3, and G10MnMoV6-3 is harder (205 HB vs 160 HB). 35# conducts heat better (49 W/m·K vs 42 W/m·K). On the shop floor, G10MnMoV6-3 welds better (very good vs good) and 35# sits in a lower cost tier (budget, $) than G10MnMoV6-3 (standard, $$).
35#Choose it when the part is bent, formed or impact-loaded, or when cost is the deciding factor.
G10MnMoV6-3Choose it when strength drives the design, or when it will be welded.
35# vs G10MnMoV6-3: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Compressive Strength
Hardness, Rockwell C
Same in both: Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Fatigue Strength (Endurance Limit) 250 MPa36.3 ksi
Physical
Density and transition temperatures.
Melting Point (Solidus)
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Min Service Temperature
Same in both: Max Service Temperature (continuous) 400°C752 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 11
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 35# | G10MnMoV6-3 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | HR | — |
| Relative cost | $ Budget | $$ Standard |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| HVOF Coating | Yes | — |
| Hot-Dip Galvanizing | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
35# vs G10MnMoV6-3 — frequently asked
Is G10MnMoV6-3 stronger than 35#?
Yes. G10MnMoV6-3 has a typical yield strength of 540 MPa (78.3 ksi) against 330 MPa (47.9 ksi) for 35# — about 64% more. Tensile strength is 690 MPa (100 ksi) vs 560 MPa (81.2 ksi).
Which is cheaper, 35# or G10MnMoV6-3?
35# is the lower-cost material: it sits in the budget tier ($) while G10MnMoV6-3 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 35# or G10MnMoV6-3?
35#, by a small margin. Both rate good for machinability — 60/100 against 55/100 for G10MnMoV6-3; for welding the order is G10MnMoV6-3 first (very good, 72/100) then 35# (good, 55/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 35# and G10MnMoV6-3 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.