Steel 30CrMo vs 60Si2Mn
Steel · grade comparison
Steel 30CrMo and 60Si2Mn are both steel grades. Both yield at about 500 MPa — strength does not separate them. 30CrMo is the more ductile: elongation 18% versus 15% for 60Si2Mn, and 60Si2Mn is harder (255 HB vs 215 HB). 30CrMo runs hotter in service (400°C vs 200°C continuous). On the shop floor, 30CrMo welds better (good vs poor).
30CrMoChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
30CrMo vs 60Si2Mn: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Poisson's Ratio 0.29 · Tensile Strength (Ultimate) 800 MPa116 ksi · Shear Strength 500 MPa72.5 ksi · Fatigue Strength (Endurance Limit) 360 MPa52.2 ksi
Physical
Density and transition temperatures.
Density
Liquidus Temperature
Same in both: Melting Point (Solidus) 1,420°C2,588 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 30 MJ/kg12,898 BTU/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 13
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 30CrMo | 60Si2Mn |
|---|---|---|
| Default condition | HR | Annealed |
| Relative cost | $$ Standard | $$ Standard |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining and Sheet metal. Both take the same 38 finishes: AlCrN, AlTiN, Black Oxide, CVD Al2O3, CVD TiCN, CVD TiN, Cerakote, Chrome Plating, Copper Plating, CrN, DLC, E-Coating and 26 more.
30CrMo vs 60Si2Mn — frequently asked
What is the difference between 30CrMo and 60Si2Mn?
Steel 30CrMo and 60Si2Mn are both steel grades. Both yield at about 500 MPa — strength does not separate them. 30CrMo is the more ductile: elongation 18% versus 15% for 60Si2Mn, and 60Si2Mn is harder (255 HB vs 215 HB).
Which is cheaper, 30CrMo or 60Si2Mn?
Both sit in the same relative cost tier ($$, standard); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 30CrMo or 60Si2Mn?
30CrMo, by a small margin. Both rate fair for machinability — 54/100 against 45/100 for 60Si2Mn; for welding the order is 30CrMo first (good, 60/100) then 60Si2Mn (poor, 20/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 30CrMo and 60Si2Mn side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.