Steel 20Cr2Ni4 vs 4620
Steel · grade comparison
Steel 20Cr2Ni4 and 4620 are both steel grades. 20Cr2Ni4 is the stronger of the two: yield strength 680 MPa (98.6 ksi) against 360 MPa (52.2 ksi) for 4620, about 89% more; tensile strength follows at 880 MPa (128 ksi) vs 570 MPa (82.7 ksi). In exchange, 4620 is the more ductile: elongation 26% versus 16% for 20Cr2Ni4, and 20Cr2Ni4 is harder (240 HB vs 163 HB). 4620 conducts heat better (46 W/m·K vs 33 W/m·K). On the shop floor, 4620 machines more easily (good vs fair) and 4620 welds better (good vs poor).
20Cr2Ni4Choose it when strength drives the design.
4620Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
20Cr2Ni4 vs 4620: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Hardness, Rockwell B
Same in both: Shear Modulus 80 GPa11.6 Msi · Poisson's Ratio 0.29 · Charpy V-Notch Impact (RT) 85 J62.7 ft·lbf
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Min Service Temperature
Same in both: Latent Heat of Fusion 250 J/g107 BTU/lb · Max Service Temperature (continuous) 400°C752 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Electrical Conductivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 30%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 20Cr2Ni4 | 4620 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | — | HR |
| Relative cost | $$ Standard | $$ Standard |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| E-Coating | — | Yes |
| HVOF Coating | — | Yes |
| Hot-Dip Galvanizing | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
20Cr2Ni4 vs 4620 — frequently asked
Is 20Cr2Ni4 stronger than 4620?
Yes. 20Cr2Ni4 has a typical yield strength of 680 MPa (98.6 ksi) against 360 MPa (52.2 ksi) for 4620 — about 89% more. Tensile strength is 880 MPa (128 ksi) vs 570 MPa (82.7 ksi).
Which is cheaper, 20Cr2Ni4 or 4620?
Both sit in the same relative cost tier ($$, standard); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 20Cr2Ni4 or 4620?
4620. Its machinability rates good (57/100) against fair (42/100) for 20Cr2Ni4; for welding the order is 4620 first (good, 65/100) then 20Cr2Ni4 (poor, 30/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 20Cr2Ni4 and 4620 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.