Steel 18Ni(190) vs Maraging 300
Steel · grade comparison
Steel 18Ni(190) and Maraging 300 are both steel grades. 18Ni(190) is the stronger of the two: yield strength 1,280 MPa (186 ksi) against 800 MPa (116 ksi) for Maraging 300, about 60% more; tensile strength follows at 1,330 MPa (193 ksi) vs 1,010 MPa (146 ksi). In exchange, Maraging 300 is the more ductile: elongation 17% versus 14% for 18Ni(190), and 18Ni(190) is harder (375 HB vs 300 HB). 18Ni(190) is stiffer (190 GPa vs 180 GPa) and 18Ni(190) conducts electricity better (3.8 % IACS vs 2.9 % IACS). On the shop floor, Maraging 300 machines more easily (45 vs 35 out of 100) and Maraging 300 sits in a lower cost tier (standard, $$) than 18Ni(190) (high, $$$$).
18Ni(190)Choose it when strength drives the design.
Maraging 300Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
18Ni(190) vs Maraging 300: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Liquidus Temperature
Same in both: Density 8 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,413°C2,575 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Same in both: Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 25 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Castability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 18Ni(190) | Maraging 300 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| 3D printing | — | Yes |
| Default condition | — | Annealed |
| Relative cost | $$$$ High | $$ Standard |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| E-Coating | — | Yes |
| HVOF Coating | — | Yes |
| Hot-Dip Galvanizing | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
18Ni(190) vs Maraging 300 — frequently asked
Is 18Ni(190) stronger than Maraging 300?
Yes. 18Ni(190) has a typical yield strength of 1,280 MPa (186 ksi) against 800 MPa (116 ksi) for Maraging 300 — about 60% more. Tensile strength is 1,330 MPa (193 ksi) vs 1,010 MPa (146 ksi).
Which is cheaper, 18Ni(190) or Maraging 300?
Maraging 300 is the lower-cost material: it sits in the standard tier ($$) while 18Ni(190) is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 18Ni(190) or Maraging 300?
Maraging 300, by a small margin. Both rate fair for machinability — 45/100 against 35/100 for 18Ni(190); for welding the order is 18Ni(190) first (excellent, 85/100) then Maraging 300 (very good, 80/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 18Ni(190) and Maraging 300 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.