Steel 18Cr2Ni4WA vs 4620
Steel · grade comparison
Steel 18Cr2Ni4WA and 4620 are both steel grades. 18Cr2Ni4WA is the stronger of the two: yield strength 1,150 MPa (167 ksi) against 360 MPa (52.2 ksi) for 4620, about 3.2 times as much; tensile strength follows at 1,350 MPa (196 ksi) vs 570 MPa (82.7 ksi). In exchange, 4620 is the more ductile: elongation 26% versus 13% for 18Cr2Ni4WA, and 18Cr2Ni4WA is harder (400 HB vs 163 HB). 4620 runs hotter in service (400°C vs 180°C continuous) and 4620 conducts heat better (46 W/m·K vs 30 W/m·K). On the shop floor, 4620 machines more easily (good vs poor), 4620 welds better (good vs poor), and 4620 sits in a lower cost tier (standard, $$) than 18Cr2Ni4WA (premium, $$$).
18Cr2Ni4WAChoose it when strength drives the design.
4620Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
18Cr2Ni4WA vs 4620: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Hardness, Rockwell B
Same in both: Reduction in Area 55%
Physical
Density and transition temperatures.
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 18Cr2Ni4WA | 4620 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | — | HR |
| Relative cost | $$$ Premium | $$ Standard |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| E-Coating | — | Yes |
| HVOF Coating | — | Yes |
| Hot-Dip Galvanizing | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
18Cr2Ni4WA vs 4620 — frequently asked
Is 18Cr2Ni4WA stronger than 4620?
Yes. 18Cr2Ni4WA has a typical yield strength of 1,150 MPa (167 ksi) against 360 MPa (52.2 ksi) for 4620 — about 3.2 times as much. Tensile strength is 1,350 MPa (196 ksi) vs 570 MPa (82.7 ksi).
Which is cheaper, 18Cr2Ni4WA or 4620?
4620 is the lower-cost material: it sits in the standard tier ($$) while 18Cr2Ni4WA is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 18Cr2Ni4WA or 4620?
4620. Its machinability rates good (57/100) against poor (20/100) for 18Cr2Ni4WA; for welding the order is 4620 first (good, 65/100) then 18Cr2Ni4WA (poor, 20/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 18Cr2Ni4WA and 4620 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.