Steel 1115 vs 1117
Steel · grade comparison
Steel 1115 and 1117 are both steel grades. 1115 is the stronger of the two: yield strength 410 MPa (59.5 ksi) against 235 MPa (34.1 ksi) for 1117, about 74% more; tensile strength follows at 480 MPa (69.6 ksi) vs 425 MPa (61.6 ksi). In exchange, 1117 is the more ductile: elongation 33% versus 15% for 1115, and 1115 is harder (143 HB vs 121 HB). On the shop floor, 1115 machines more easily (80 vs 70 out of 100) and 1117 welds better (50 vs 40 out of 100).
1115Choose it when strength drives the design, or when the part is machined in volume.
1117Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
1115 vs 1117: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Liquidus Temperature
Same in both: Density 7.87 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F
Thermal
How each material carries heat and how hot it can run.
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Same in both: Thermal Conductivity 51 W/m·K29.5 BTU/hr·ft·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 10.8 % IACS · Electrical Resistivity 1.6×10⁻⁷ Ω·m6.3 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Same in both: Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 30%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 25.4 MN·m/kg
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1115 | 1117 |
|---|---|---|
| CNC machining | — | Yes |
| Default condition | — | HR |
| Relative cost | $ Budget | $ Budget |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| E-Coating | — | Yes |
| HVOF Coating | — | Yes |
| Hot-Dip Galvanizing | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
1115 vs 1117 — frequently asked
Is 1115 stronger than 1117?
Yes. 1115 has a typical yield strength of 410 MPa (59.5 ksi) against 235 MPa (34.1 ksi) for 1117 — about 74% more. Tensile strength is 480 MPa (69.6 ksi) vs 425 MPa (61.6 ksi).
Which is cheaper, 1115 or 1117?
Both sit in the same relative cost tier ($, budget); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 1115 or 1117?
1115, by a small margin. Both rate very good for machinability — 80/100 against 70/100 for 1117; for welding the order is 1117 first (fair, 50/100) then 1115 (fair, 40/100).