Steel 1.0031 vs 1006
Steel · grade comparison
Steel 1.0031 and 1006 are both steel grades. 1.0031 is the stronger of the two: yield strength 190 MPa (27.6 ksi) against 170 MPa (24.7 ksi) for 1006, about 12% more. 1.0031 is harder — 95 HV against 90 HV for 1006 — which matters for wear surfaces and threads. 1006 runs hotter in service (400°C vs 350°C continuous) and 1006 conducts heat better (65 W/m·K vs 52 W/m·K). On the shop floor, 1.0031 machines more easily (good vs fair) and 1006 forms better (95 vs 85 out of 100).
1.0031Choose it when strength drives the design, or when surface hardness matters.
1006Choose it when the part sees heat.
1.0031 vs 1006: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Tensile Strength (Ultimate) 300 MPa43.5 ksi · Shear Strength 200 MPa29 ksi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Castability
Same in both: Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb
Common Calculations
Ratios derived from the values above.
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Strength (UTS / density) 38 kN·m/kg
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.0031 | 1006 |
|---|---|---|
| Sheet metal | — | Yes |
| Default condition | — | HR |
| Relative cost | $ Budget | $ Budget |
| Min. machined wall | — | — |
| Best machined surface | — | — |
| Black Oxide | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| E-Coating | — | Yes |
| Hot-Dip Galvanizing | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
| Powder Coating | — | Yes |
| Tin Plating | — | Yes |
| Zinc Plating | — | Yes |
| Zinc-Flake (Dip-Spin) Coating | — | Yes |
| Zinc-Nickel Plating | — | Yes |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
1.0031 vs 1006 — frequently asked
Is 1.0031 stronger than 1006?
Yes. 1.0031 has a typical yield strength of 190 MPa (27.6 ksi) against 170 MPa (24.7 ksi) for 1006 — about 12% more. Tensile strength is 300 MPa (43.5 ksi) vs 300 MPa (43.5 ksi).
Which is cheaper, 1.0031 or 1006?
Both sit in the same relative cost tier ($, budget); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 1.0031 or 1006?
1.0031. Its machinability rates good (58/100) against fair (45/100) for 1006.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.0031 and 1006 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.