Steel 1006 vs 1015
Steel · grade comparison
Steel 1006 and 1015 are both steel grades, both low carbon steel. 1015 is the stronger of the two: yield strength 190 MPa (27.6 ksi) against 170 MPa (24.7 ksi) for 1006, about 12% more; tensile strength follows at 345 MPa (50 ksi) vs 300 MPa (43.5 ksi). 1015 is harder — 101 HB against 86 HB for 1006 — which matters for wear surfaces and threads. 1006 conducts heat better (65 W/m·K vs 51.9 W/m·K). On the shop floor, 1006 forms better (95 vs 85 out of 100).
1015Choose it when strength drives the design, or when surface hardness matters.
1006 vs 1015: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Compressive Strength
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.87 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Same in both: Latent Heat of Fusion 247 J/g106 BTU/lb · Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 26 MN·m/kg
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1006 | 1015 |
|---|---|---|
| CNC machining | — | Yes |
| Default condition | HR | HR |
| Relative cost | $ Budget | $ Budget |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| HVOF Coating | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| TiAlN | — | Yes |
| TiB2 | — | Yes |
| TiCN | — | Yes |
| TiN | — | Yes |
| WC/C | — | Yes |
| ZrN | — | Yes |
Both are offered for Sheet metal. They share 22 finishes: Black Oxide, Cerakote, Chrome Plating, Copper Plating, E-Coating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Hot-Dip Galvanizing, Manganese Phosphate, Nickel Plating and 10 more.
1006 vs 1015 — frequently asked
Is 1015 stronger than 1006?
Yes. 1015 has a typical yield strength of 190 MPa (27.6 ksi) against 170 MPa (24.7 ksi) for 1006 — about 12% more. Tensile strength is 345 MPa (50 ksi) vs 300 MPa (43.5 ksi).
Which is cheaper, 1006 or 1015?
Both sit in the same relative cost tier ($, budget); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 1006 or 1015?
1015, by a small margin. Both rate fair for machinability — 52/100 against 45/100 for 1006.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1006 and 1015 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.