Stainless Steel V-57 CD+A vs V-57-STA
Stainless Steel · V-57 temper comparison
V-57 CD+A and V-57-STA are two conditions of the same stainless steel grade, V-57: CD+A (cold drawn/cold worked then aged) versus STA (solution treated and aged). The chemistry is identical, so every difference below comes from the condition. V-57 CD+A is the stronger of the two: yield strength 1,035 MPa (150 ksi) against 725 MPa (105 ksi) for V-57-STA, about 43% more; tensile strength follows at 1,240 MPa (180 ksi) vs 1,070 MPa (155 ksi). In exchange, V-57-STA is the more ductile: elongation 20% versus 12% for V-57 CD+A, and V-57 CD+A is harder (352 HB vs 302 HB). V-57-STA runs hotter in service (650°C vs 565°C continuous). On the shop floor, V-57-STA welds better (fair vs poor).
V-57 CD+AChoose it when strength drives the design.
V-57-STAChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
V-57 CD+A vs V-57-STA: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Same in both: Elastic (Young's) Modulus 201 GPa29.2 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 165 GPa23.9 Msi · Poisson's Ratio 0.31 · Compressive Strength 745 MPa108 ksi · Fracture Toughness (K_IC) 130 MPa·√m118 ksi·√in · Hardness, Vickers 320 HV
Physical
Density and transition temperatures.
Same in both: Density 7.92 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,370°C2,498 °F · Liquidus Temperature 1,425°C2,597 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 14 W/m·K8.1 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.5 µm/m·K9.2 µin/in·°F · Latent Heat of Fusion 285 J/g123 BTU/lb · Min Service Temperature -253°C-423 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 1.9 % IACS · Electrical Resistivity 9.1×10⁻⁷ Ω·m35.8 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V · Corrosion Resistance 62 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 15% · Brazeability / Solderability 40 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 95 MJ/kg40,843 BTU/lb · Embodied Carbon (primary production) 6.8 kg CO₂/kg · Embodied Water 200 L/kg24 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
V-57 CD+A vs V-57-STA — frequently asked
Is V-57 CD+A stronger than V-57-STA?
Yes. V-57 CD+A has a typical yield strength of 1,035 MPa (150 ksi) against 725 MPa (105 ksi) for V-57-STA — about 43% more. Tensile strength is 1,240 MPa (180 ksi) vs 1,070 MPa (155 ksi).
Which condition does FabDigit quote by default, CD+A or STA?
STA is the default V-57 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, V-57 CD+A or V-57-STA?
V-57-STA, by a small margin. Both rate poor for machinability — 20/100 against 15/100 for V-57 CD+A; for welding the order is V-57-STA first (fair, 40/100) then V-57 CD+A (poor, 25/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in V-57 CD+A and V-57-STA side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.