Stainless Steel S41041 1/4H vs S41041 Annealed
Stainless Steel · S41041 temper comparison
S41041 1/4H and S41041 Annealed are two conditions of the same stainless steel grade, S41041: 1/4H (quarter hard) versus Annealed. The chemistry is identical, so every difference below comes from the condition. S41041 1/4H is the stronger of the two: yield strength 500 MPa (72.5 ksi) against 280 MPa (40.6 ksi) for S41041 Annealed, about 79% more; tensile strength follows at 620 MPa (89.9 ksi) vs 450 MPa (65.3 ksi). In exchange, S41041 Annealed is the more ductile: elongation 30% versus 12% for S41041 1/4H, and S41041 1/4H is harder (210 HB vs 150 HB). S41041 Annealed runs hotter in service (650°C vs 400°C continuous).
S41041 1/4HChoose it when strength drives the design.
S41041 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
S41041 1/4H vs S41041 Annealed: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 78 GPa11.3 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,480°C2,696 °F · Liquidus Temperature 1,530°C2,786 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 25 W/m·K14.4 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.5 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 3 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 45 / 100 · Brazeability / Solderability 55 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 42 MJ/kg18,057 BTU/lb · Embodied Carbon (primary production) 3.2 kg CO₂/kg · Embodied Water 140 L/kg16.8 gal/lb · Typical Recycled Content 70%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
S41041 1/4H vs S41041 Annealed — frequently asked
Is S41041 1/4H stronger than S41041 Annealed?
Yes. S41041 1/4H has a typical yield strength of 500 MPa (72.5 ksi) against 280 MPa (40.6 ksi) for S41041 Annealed — about 79% more. Tensile strength is 620 MPa (89.9 ksi) vs 450 MPa (65.3 ksi).
Which condition does FabDigit quote by default, 1/4H or Annealed?
Annealed is the default S41041 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose S41041 1/4H over S41041 Annealed?
Pick S41041 1/4H when strength drives the design. Pick S41041 Annealed when the part is bent, formed or impact-loaded, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in S41041 1/4H and S41041 Annealed side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.