Stainless Steel Nitronic 60 vs S30V
Stainless Steel · grade comparison
Stainless Steel Nitronic 60 and S30V are both stainless steel grades, both wear resistant ss. S30V is the stronger of the two: yield strength 620 MPa (89.9 ksi) against 414 MPa (60 ksi) for Nitronic 60, about 50% more; tensile strength follows at 900 MPa (131 ksi) vs 717 MPa (104 ksi). In exchange, Nitronic 60 is the more ductile: elongation 60% versus 10% for S30V, and S30V is harder (255 HB vs 210 HB). S30V is stiffer (214 GPa vs 196 GPa) and Nitronic 60 runs hotter in service (870°C vs 300°C continuous). On the shop floor, Nitronic 60 welds better (very good vs not recommended).
Nitronic 60Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
S30VChoose it when strength drives the design.
Nitronic 60 vs S30V: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Hardness, Rockwell C
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Carbon (primary production) 4.5 kg CO₂/kg
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Nitronic 60 | S30V |
|---|---|---|
| Sheet metal | Yes | — |
| Default condition | Solution Annealed | Annealed |
| Relative cost | $$$$$ Specialty | $$$$$ Specialty |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining. Both take the same 32 finishes: AlCrN, AlTiN, Black Oxide, CVD Al2O3, CVD TiCN, CVD TiN, Cerakote, Chrome Plating, CrN, DLC, Electroless Nickel (EN), Electropolishing and 20 more.
Nitronic 60 vs S30V — frequently asked
Is S30V stronger than Nitronic 60?
Yes. S30V has a typical yield strength of 620 MPa (89.9 ksi) against 414 MPa (60 ksi) for Nitronic 60 — about 50% more. Tensile strength is 900 MPa (131 ksi) vs 717 MPa (104 ksi).
Which is cheaper, Nitronic 60 or S30V?
Both sit in the same relative cost tier ($$$$$, specialty); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which welds better, Nitronic 60 or S30V?
Nitronic 60. Its weldability rates very good (72/100) against not recommended (10/100) for S30V.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Nitronic 60 and S30V side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.