Stainless Steel E2209T1-1 and ER308H are both stainless steel grades. E2209T1-1 is the stronger of the two: yield strength 600 MPa (87 ksi) against 415 MPa (60.2 ksi) for ER308H, about 45% more; tensile strength follows at 810 MPa (117 ksi) vs 590 MPa (85.6 ksi). In exchange, ER308H is the more ductile: elongation 38% versus 26% for E2209T1-1, and E2209T1-1 is harder (250 HB vs 175 HB). ER308H runs hotter in service (800°C vs 250°C continuous) and ER308H conducts electricity better (2.4 % IACS vs 2 % IACS). On the shop floor, ER308H machines more easily (fair vs poor) and ER308H sits in a lower cost tier (premium, $$$) than E2209T1-1 (high, $$$$).
E2209T1-1Choose it when strength drives the design.
ER308HChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
E2209T1-1 vs ER308H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Hardness, Rockwell B
Same in both: Shear Modulus 77 GPa11.2 Msi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Same in both: Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Same in both: Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Typical Recycled Content
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 4.5 kg CO₂/kg · Embodied Water 130 L/kg15.6 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | E2209T1-1 | ER308H |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
E2209T1-1 vs ER308H — frequently asked
Is E2209T1-1 stronger than ER308H?
Yes. E2209T1-1 has a typical yield strength of 600 MPa (87 ksi) against 415 MPa (60.2 ksi) for ER308H — about 45% more. Tensile strength is 810 MPa (117 ksi) vs 590 MPa (85.6 ksi).
Which is cheaper, E2209T1-1 or ER308H?
ER308H is the lower-cost material: it sits in the premium tier ($$$) while E2209T1-1 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, E2209T1-1 or ER308H?
ER308H. Its machinability rates fair (38/100) against poor (28/100) for E2209T1-1; for welding the order is ER308H first (excellent, 88/100) then E2209T1-1 (very good, 80/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in E2209T1-1 and ER308H side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.