Stainless Steel 409 vs S43037
Stainless Steel · grade comparison
Stainless Steel 409 and S43037 are both stainless steel grades. S43037 is the stronger of the two: yield strength 285 MPa (41.3 ksi) against 250 MPa (36.3 ksi) for 409, about 14% more; tensile strength follows at 480 MPa (69.6 ksi) vs 450 MPa (65.3 ksi). S43037 runs hotter in service (815°C vs 675°C continuous). On the shop floor, 409 machines more easily (good vs fair) and S43037 sits in a lower cost tier (standard, $$) than 409 (premium, $$$).
409Choose it when the part is machined in volume.
S43037Choose it when strength drives the design, or when the part sees heat.
409 vs S43037: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Vickers
Fracture Toughness (K_IC)
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Elongation at Break 30% · Reduction in Area 65% · Hardness, Brinell 150 HB · Hardness, Rockwell B 80 HRB
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.7 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Latent Heat of Fusion 260 J/g112 BTU/lb
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.9 % IACS · Electrical Resistivity 6×10⁻⁷ Ω·m23.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Brazeability / Solderability
Polishability
Castability
Same in both: Formability (cold) 78 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 26 MN·m/kg
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 409 | S43037 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | Annealed | — |
| Relative cost | $$$ Premium | $$ Standard |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Passivation (Stainless Steel) | Yes | — |
They share 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
409 vs S43037 — frequently asked
Is S43037 stronger than 409?
Yes. S43037 has a typical yield strength of 285 MPa (41.3 ksi) against 250 MPa (36.3 ksi) for 409 — about 14% more. Tensile strength is 480 MPa (69.6 ksi) vs 450 MPa (65.3 ksi).
Which is cheaper, 409 or S43037?
S43037 is the lower-cost material: it sits in the standard tier ($$) while 409 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 409 or S43037?
409. Its machinability rates good (55/100) against fair (45/100) for S43037.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 409 and S43037 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.