Stainless Steel 15-7 Mo Condition A vs 15-7 Mo-TH1050
Stainless Steel · 15-7 Mo temper comparison
15-7 Mo Condition A and 15-7 Mo-TH1050 are two conditions of the same stainless steel grade, 15-7 Mo: Condition A (solution annealed) versus TH1050 (austenite conditioned at 760 °C, cooled, then aged 566 °C). The chemistry is identical, so every difference below comes from the condition. 15-7 Mo-TH1050 is the stronger of the two: yield strength 1,345 MPa (195 ksi) against 415 MPa (60.2 ksi) for 15-7 Mo Condition A, about 3.2 times as much; tensile strength follows at 1,415 MPa (205 ksi) vs 950 MPa (138 ksi). In exchange, 15-7 Mo Condition A is the more ductile: elongation 25% versus 7% for 15-7 Mo-TH1050, and 15-7 Mo-TH1050 is harder (45 HRC vs 13 HRC). On the shop floor, 15-7 Mo Condition A machines more easily (fair vs poor).
15-7 Mo Condition AChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
15-7 Mo-TH1050Choose it when strength drives the design.
15-7 Mo Condition A vs 15-7 Mo-TH1050: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
15-7 Mo Condition A15-7 Mo-TH1050
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Rockwell C
Hardness, Vickers
Same in both: Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Hardness, Brinell 200 HB · Hardness, Rockwell B 92 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.8 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,440°C2,624 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 16 W/m·K9.2 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.5 µm/m·K6.4 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 425°C797 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.1 % IACS · Electrical Resistivity 8.3×10⁻⁷ Ω·m32.7 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 50 / 100 · Brazeability / Solderability 40 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 68 MJ/kg29,235 BTU/lb · Embodied Carbon (primary production) 5.4 kg CO₂/kg · Embodied Water 200 L/kg24 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
15-7 Mo Condition A vs 15-7 Mo-TH1050 — frequently asked
Is 15-7 Mo-TH1050 stronger than 15-7 Mo Condition A?
Yes. 15-7 Mo-TH1050 has a typical yield strength of 1,345 MPa (195 ksi) against 415 MPa (60.2 ksi) for 15-7 Mo Condition A — about 3.2 times as much. Tensile strength is 1,415 MPa (205 ksi) vs 950 MPa (138 ksi).
Which condition does FabDigit quote by default, Condition A or TH1050?
Condition A is the default 15-7 Mo condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 15-7 Mo Condition A or 15-7 Mo-TH1050?
15-7 Mo Condition A. Its machinability rates fair (45/100) against poor (28/100) for 15-7 Mo-TH1050.