Stainless Steel 1.4652 Annealed vs 1.4652-CD
Stainless Steel · 1.4652 temper comparison
1.4652 Annealed and 1.4652-CD are two conditions of the same stainless steel grade, 1.4652: Annealed versus CD (cold drawn). The chemistry is identical, so every difference below comes from the condition. 1.4652-CD is the stronger of the two: yield strength 700 MPa (102 ksi) against 480 MPa (69.6 ksi) for 1.4652 Annealed, about 46% more; tensile strength follows at 950 MPa (138 ksi) vs 800 MPa (116 ksi). In exchange, 1.4652 Annealed is the more ductile: elongation 50% versus 25% for 1.4652-CD, and 1.4652-CD is harder (300 HB vs 210 HB). 1.4652 Annealed runs hotter in service (400°C vs 350°C continuous).
1.4652 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1.4652-CDChoose it when strength drives the design.
1.4652 Annealed vs 1.4652-CD: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 195 GPa28.3 Msi · Shear Modulus 75 GPa10.9 Msi · Bulk Modulus 163 GPa23.6 Msi · Poisson's Ratio 0.3 · Hardness, Rockwell B 95 HRB
Physical
Density and transition temperatures.
Same in both: Density 8 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,320°C2,408 °F · Liquidus Temperature 1,400°C2,552 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 8.5 W/m·K4.9 BTU/hr·ft·°F · Specific Heat Capacity 510 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.5 µm/m·K9.2 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 2.2 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 50 / 100 · Polishability 78 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 85 MJ/kg36,543 BTU/lb · Embodied Carbon (primary production) 5.8 kg CO₂/kg · Embodied Water 200 L/kg24 gal/lb · Typical Recycled Content 45%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4652 Annealed vs 1.4652-CD — frequently asked
Is 1.4652-CD stronger than 1.4652 Annealed?
Yes. 1.4652-CD has a typical yield strength of 700 MPa (102 ksi) against 480 MPa (69.6 ksi) for 1.4652 Annealed — about 46% more. Tensile strength is 950 MPa (138 ksi) vs 800 MPa (116 ksi).
Which condition does FabDigit quote by default, Annealed or CD?
Annealed is the default 1.4652 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, 1.4652 Annealed or 1.4652-CD?
1.4652 Annealed. Its weldability rates good (65/100) against good (60/100) for 1.4652-CD.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4652 Annealed and 1.4652-CD side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.