Stainless Steel 1.4597 vs 304
Stainless Steel · grade comparison
Stainless Steel 1.4597 and 304 are both stainless steel grades. 1.4597 is the stronger of the two: yield strength 340 MPa (49.3 ksi) against 250 MPa (36.3 ksi) for 304, about 36% more; tensile strength follows at 720 MPa (104 ksi) vs 585 MPa (84.8 ksi). 1.4597 is harder — 195 HB against 150 HB for 304 — which matters for wear surfaces and threads. 304 runs hotter in service (870°C vs 760°C continuous). On the shop floor, 304 welds better (excellent vs good), 304 forms better (excellent vs very good), and 1.4597 sits in a lower cost tier (budget, $) than 304 (standard, $$).
1.4597Choose it when strength drives the design, or when surface hardness matters.
304Choose it when the part sees heat, or when it will be welded.
1.4597 vs 304: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 77 GPa11.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Density
Same in both: Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,450°C2,642 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.4 % IACS · Electrical Resistivity 7.2×10⁻⁷ Ω·m28.3 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Same in both: Machinability Rating (AISI 1212 = 100 %) 45%
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Same in both: Thermal Diffusivity 4.1 mm²/s · Thermal Shock Resistance Index 3
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.4597 | 304 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Casting & forging | — | Yes |
| Default condition | — | Annealed |
| Relative cost | $ Budget | $$ Standard |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| Electropolishing | — | Yes |
| HVOF Coating | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
| Passivation (Stainless Steel) | — | Yes |
They share 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
1.4597 vs 304 — frequently asked
Is 1.4597 stronger than 304?
Yes. 1.4597 has a typical yield strength of 340 MPa (49.3 ksi) against 250 MPa (36.3 ksi) for 304 — about 36% more. Tensile strength is 720 MPa (104 ksi) vs 585 MPa (84.8 ksi).
Which is cheaper, 1.4597 or 304?
1.4597 is the lower-cost material: it sits in the budget tier ($) while 304 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 1.4597 or 304?
304, by a small margin. Both rate fair for machinability — 45/100 against 38/100 for 1.4597; for welding the order is 304 first (excellent, 88/100) then 1.4597 (good, 65/100).