Stainless Steel 1.4580 vs 304
Stainless Steel · grade comparison
Stainless Steel 1.4580 and 304 are both stainless steel grades. Both yield at about 260 MPa — strength does not separate them. 304 is the more ductile: elongation 55% versus 45% for 1.4580, and 1.4580 is harder (165 HB vs 150 HB). 304 runs hotter in service (870°C vs 800°C continuous). On the shop floor, 304 sits in a lower cost tier (standard, $$) than 1.4580 (premium, $$$).
304Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1.4580 vs 304: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Shear Modulus 77 GPa11.2 Msi · Fatigue Strength (Endurance Limit) 250 MPa36.3 ksi · Fracture Toughness (K_IC) 220 MPa·√m200 ksi·√in · Hardness, Rockwell B 82 HRB
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 8 g/cm³0.29 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 53 MJ/kg22,786 BTU/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 3
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.4580 | 304 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Casting & forging | — | Yes |
| Default condition | — | Annealed |
| Relative cost | $$$ Premium | $$ Standard |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| Electropolishing | — | Yes |
| HVOF Coating | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
| Passivation (Stainless Steel) | — | Yes |
They share 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
1.4580 vs 304 — frequently asked
What is the difference between 1.4580 and 304?
Stainless Steel 1.4580 and 304 are both stainless steel grades. Both yield at about 260 MPa — strength does not separate them. 304 is the more ductile: elongation 55% versus 45% for 1.4580, and 1.4580 is harder (165 HB vs 150 HB).
Which is cheaper, 1.4580 or 304?
304 is the lower-cost material: it sits in the standard tier ($$) while 1.4580 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 1.4580 or 304?
304, by a small margin. Both rate fair for machinability — 45/100 against 38/100 for 1.4580.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4580 and 304 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.