Stainless Steel 1.4530 vs 15-5 PH
Stainless Steel · grade comparison
Stainless Steel 1.4530 and 15-5 PH are both stainless steel grades. 1.4530 is the stronger of the two: yield strength 1,200 MPa (174 ksi) against 795 MPa (115 ksi) for 15-5 PH, about 51% more; tensile strength follows at 1,300 MPa (189 ksi) vs 1,030 MPa (149 ksi). 1.4530 is harder — 390 HB against 311 HB for 15-5 PH — which matters for wear surfaces and threads. 1.4530 runs hotter in service (400°C vs 300°C continuous). On the shop floor, 15-5 PH machines more easily (fair vs poor), 15-5 PH forms better (fair vs poor), and 1.4530 sits in a lower cost tier (high, $$$$) than 15-5 PH (specialty, $$$$$).
1.4530Choose it when strength drives the design, or when surface hardness matters.
15-5 PHChoose it when the part is machined in volume.
1.4530 vs 15-5 PH: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Shear Modulus 77 GPa11.2 Msi · Elongation at Break 14%
Physical
Density and transition temperatures.
Liquidus Temperature
Same in both: Density 7.8 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Latent Heat of Fusion 270 J/g116 BTU/lb
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.2 % IACS · Electrical Resistivity 8×10⁻⁷ Ω·m31.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Same in both: Brazeability / Solderability 45 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.4530 | 15-5 PH |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| 3D printing | — | Yes |
| Default condition | — | Condition A |
| Relative cost | $$$$ High | $$$$$ Specialty |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| Electropolished (Metal AM) | — | Yes |
| Electropolishing | — | Yes |
| HVOF Coating | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
They share 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
1.4530 vs 15-5 PH — frequently asked
Is 1.4530 stronger than 15-5 PH?
Yes. 1.4530 has a typical yield strength of 1,200 MPa (174 ksi) against 795 MPa (115 ksi) for 15-5 PH — about 51% more. Tensile strength is 1,300 MPa (189 ksi) vs 1,030 MPa (149 ksi).
Which is cheaper, 1.4530 or 15-5 PH?
1.4530 is the lower-cost material: it sits in the high tier ($$$$) while 15-5 PH is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 1.4530 or 15-5 PH?
15-5 PH. Its machinability rates fair (42/100) against poor (30/100) for 1.4530; for welding the order is 15-5 PH first (very good, 70/100) then 1.4530 (good, 65/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4530 and 15-5 PH side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.