Stainless Steel 1.4501 vs 2205
Stainless Steel · grade comparison
Stainless Steel 1.4501 and 2205 are both stainless steel grades. 1.4501 is the stronger of the two: yield strength 580 MPa (84.1 ksi) against 540 MPa (78.3 ksi) for 2205, about 7% more. 2205 is stiffer (200 GPa vs 190 GPa) and 2205 conducts heat better (16 W/m·K vs 14.2 W/m·K). On the shop floor, 2205 machines more easily (32 vs 22 out of 100), 2205 welds better (very good vs good), and 2205 forms better (good vs fair).
1.4501Choose it when strength drives the design, or when cost is the deciding factor.
2205Choose it when the part is machined in volume, or when it will be welded.
1.4501 vs 2205: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Reduction in Area
Compressive Strength
Shear Strength
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Rockwell C
Hardness, Vickers
Same in both: Poisson's Ratio 0.3 · Elongation at Break 30% · Fatigue Strength (Endurance Limit) 390 MPa56.6 ksi · Charpy V-Notch Impact (RT) 220 J162 ft·lbf
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 5
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.4501 | 2205 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | — | Solution Annealed |
| Relative cost | $$$$ High | $$$$$ Specialty |
| Min. machined wall | — | 1 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| Electropolishing | — | Yes |
| HVOF Coating | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
| Passivation (Stainless Steel) | — | Yes |
They share 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
1.4501 vs 2205 — frequently asked
Is 1.4501 stronger than 2205?
Yes. 1.4501 has a typical yield strength of 580 MPa (84.1 ksi) against 540 MPa (78.3 ksi) for 2205 — about 7% more. Tensile strength is 800 MPa (116 ksi) vs 790 MPa (115 ksi).
Which is cheaper, 1.4501 or 2205?
1.4501 is the lower-cost material: it sits in the high tier ($$$$) while 2205 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 1.4501 or 2205?
2205, by a small margin. Both rate poor for machinability — 32/100 against 22/100 for 1.4501; for welding the order is 2205 first (very good, 78/100) then 1.4501 (good, 60/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4501 and 2205 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.