Stainless Steel 1.4470 vs CD3MCuN
Stainless Steel · grade comparison
Stainless Steel 1.4470 and CD3MCuN are both stainless steel grades. CD3MCuN is the stronger of the two: yield strength 550 MPa (79.8 ksi) against 500 MPa (72.5 ksi) for 1.4470, about 10% more; tensile strength follows at 740 MPa (107 ksi) vs 700 MPa (102 ksi). CD3MCuN runs hotter in service (300°C vs 260°C continuous). On the shop floor, 1.4470 sits in a lower cost tier (premium, $$$) than CD3MCuN (high, $$$$).
1.4470Choose it when cost is the deciding factor.
CD3MCuNChoose it when strength drives the design, or when the part sees heat.
1.4470 vs CD3MCuN: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Same in both: Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3 · Reduction in Area 45% · Fatigue Strength (Endurance Limit) 300 MPa43.5 ksi · Hardness, Brinell 230 HB · Hardness, Rockwell B 98 HRB · Hardness, Rockwell C 21 HRC · Hardness, Vickers 245 HV
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 480 J/kg·K0.11 BTU/lb·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.2 % IACS · Electrical Resistivity 8×10⁻⁷ Ω·m31.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.15 V · Corrosion Resistance 78 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 190 L/kg22.8 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.4470 | CD3MCuN |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
1.4470 vs CD3MCuN — frequently asked
Is CD3MCuN stronger than 1.4470?
Yes. CD3MCuN has a typical yield strength of 550 MPa (79.8 ksi) against 500 MPa (72.5 ksi) for 1.4470 — about 10% more. Tensile strength is 740 MPa (107 ksi) vs 700 MPa (102 ksi).
Which is cheaper, 1.4470 or CD3MCuN?
1.4470 is the lower-cost material: it sits in the premium tier ($$$) while CD3MCuN is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, 1.4470 or CD3MCuN?
1.4470. Its weldability rates very good (70/100) against good (62/100) for CD3MCuN.