1.4439-CD and 1.4439 CW-1/4H are two conditions of the same stainless steel grade, 1.4439: CD (cold drawn) versus CW-1/4H (1/4 Hard). The chemistry is identical, so every difference below comes from the condition. 1.4439 CW-1/4H is the stronger of the two: yield strength 560 MPa (81.2 ksi) against 480 MPa (69.6 ksi) for 1.4439-CD, about 17% more; tensile strength follows at 820 MPa (119 ksi) vs 720 MPa (104 ksi). In exchange, 1.4439-CD is the more ductile: elongation 30% versus 20% for 1.4439 CW-1/4H, and 1.4439 CW-1/4H is harder (250 HB vs 230 HB). 1.4439-CD runs hotter in service (400°C vs 300°C continuous).
1.4439-CDChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1.4439 CW-1/4HChoose it when strength drives the design.
1.4439-CD vs 1.4439 CW-1/4H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3 · Charpy V-Notch Impact (RT) 110 J81.1 ft·lbf
Physical
Density and transition temperatures.
Same in both: Density 8 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,370°C2,498 °F · Liquidus Temperature 1,400°C2,552 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 14 W/m·K8.1 BTU/hr·ft·°F · Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.5 µm/m·K9.2 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2 % IACS · Electrical Resistivity 8.5×10⁻⁷ Ω·m33.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V · Corrosion Resistance 78 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 55 / 100 · Polishability 72 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 62 MJ/kg26,655 BTU/lb · Embodied Carbon (primary production) 5.5 kg CO₂/kg · Embodied Water 220 L/kg26.4 gal/lb · Typical Recycled Content 45%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4439-CD vs 1.4439 CW-1/4H — frequently asked
Is 1.4439 CW-1/4H stronger than 1.4439-CD?
Yes. 1.4439 CW-1/4H has a typical yield strength of 560 MPa (81.2 ksi) against 480 MPa (69.6 ksi) for 1.4439-CD — about 17% more. Tensile strength is 820 MPa (119 ksi) vs 720 MPa (104 ksi).
Which condition does FabDigit quote by default, CD or CW-1/4H?
SA is the default 1.4439 condition in the FabDigit quote flow (neither CD nor CW-1/4H). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.4439-CD or 1.4439 CW-1/4H?
1.4439-CD. Its machinability rates fair (38/100) against poor (30/100) for 1.4439 CW-1/4H.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4439-CD and 1.4439 CW-1/4H side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.