Stainless Steel 1.4411 vs CA15M
Stainless Steel · grade comparison
Stainless Steel 1.4411 and CA15M are both stainless steel grades. 1.4411 is the stronger of the two: yield strength 620 MPa (89.9 ksi) against 550 MPa (79.8 ksi) for CA15M, about 13% more; tensile strength follows at 850 MPa (123 ksi) vs 725 MPa (105 ksi). In exchange, CA15M is the more ductile: elongation 22% versus 18% for 1.4411, and 1.4411 is harder (275 HB vs 225 HB). CA15M runs hotter in service (650°C vs 350°C continuous) and CA15M conducts heat better (24.2 W/m·K vs 17 W/m·K). On the shop floor, CA15M machines more easily (45 vs 35 out of 100) and 1.4411 welds better (very good vs fair).
1.4411Choose it when strength drives the design, or when it will be welded.
CA15MChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1.4411 vs CA15M: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Latent Heat of Fusion 270 J/g116 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Brazeability / Solderability
Polishability
Same in both: Formability (cold) 10 / 100 · Castability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.4411 | CA15M |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
1.4411 vs CA15M — frequently asked
Is 1.4411 stronger than CA15M?
Yes. 1.4411 has a typical yield strength of 620 MPa (89.9 ksi) against 550 MPa (79.8 ksi) for CA15M — about 13% more. Tensile strength is 850 MPa (123 ksi) vs 725 MPa (105 ksi).
Which is cheaper, 1.4411 or CA15M?
Both sit in the same relative cost tier ($$$, premium); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 1.4411 or CA15M?
CA15M, by a small margin. Both rate fair for machinability — 45/100 against 35/100 for 1.4411; for welding the order is 1.4411 first (very good, 70/100) then CA15M (fair, 40/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4411 and CA15M side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.