Stainless Steel 1.4112 +A vs 1.4112 QT-59
Stainless Steel · 1.4112 temper comparison
1.4112 +A and 1.4112 QT-59 are two conditions of the same stainless steel grade, 1.4112: +A (annealed) versus QT-59 (hardened + tempered 150–180 °C). The chemistry is identical, so every difference below comes from the condition. 1.4112 QT-59 is the stronger of the two: yield strength 1,850 MPa (268 ksi) against 470 MPa (68.2 ksi) for 1.4112 +A, about 3.9 times as much; tensile strength follows at 2,050 MPa (297 ksi) vs 800 MPa (116 ksi). In exchange, 1.4112 +A is the more ductile: elongation 16% versus 1.5% for 1.4112 QT-59, and 1.4112 QT-59 is harder (59 HRC vs 24 HRC). 1.4112 +A runs hotter in service (400°C vs 180°C continuous). On the shop floor, 1.4112 +A machines more easily (fair vs not recommended).
1.4112 +AChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1.4112 QT-59Choose it when strength drives the design.
1.4112 +A vs 1.4112 QT-59: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 215 GPa31.2 Msi · Shear Modulus 83 GPa12 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.28 · Reduction in Area 35% · Shear Strength 500 MPa72.5 ksi · Hardness, Brinell 250 HB
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,465°C2,669 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 15 W/m·K8.7 BTU/hr·ft·°F · Specific Heat Capacity 430 J/kg·K0.1 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.4 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 260 J/g112 BTU/lb · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.7 % IACS · Electrical Resistivity 6.5×10⁻⁷ Ω·m25.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Same in both: Machinability Rating (AISI 1212 = 100 %) 40% · Weldability 15 / 100 · Formability (cold) 20 / 100 · Castability 30 / 100 · Brazeability / Solderability 40 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 58 MJ/kg24,936 BTU/lb · Embodied Carbon (primary production) 4.8 kg CO₂/kg · Embodied Water 180 L/kg21.6 gal/lb · Typical Recycled Content 50%
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
1.4112 +A vs 1.4112 QT-59 — frequently asked
Is 1.4112 QT-59 stronger than 1.4112 +A?
Yes. 1.4112 QT-59 has a typical yield strength of 1,850 MPa (268 ksi) against 470 MPa (68.2 ksi) for 1.4112 +A — about 3.9 times as much. Tensile strength is 2,050 MPa (297 ksi) vs 800 MPa (116 ksi).
Which condition does FabDigit quote by default, +A or QT-59?
+A is the default 1.4112 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 1.4112 +A or 1.4112 QT-59?
1.4112 +A. Its machinability rates fair (35/100) against not recommended (3/100) for 1.4112 QT-59.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4112 +A and 1.4112 QT-59 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.