Stainless Steel 1.4011 vs CA40F
Stainless Steel · grade comparison
Stainless Steel 1.4011 and CA40F are both stainless steel grades. Both yield at about 550 MPa — strength does not separate them. 1.4011 is the more ductile: elongation 22% versus 14% for CA40F, and CA40F is harder (240 HB vs 225 HB). On the shop floor, CA40F machines more easily (good vs fair) and 1.4011 welds better (fair vs poor).
1.4011Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
CA40FChoose it when the part is machined in volume.
1.4011 vs CA40F: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.28 · Tensile Strength (Ultimate) 760 MPa110 ksi · Shear Strength 460 MPa66.7 ksi
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.61 g/cm³0.27 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 3 % IACS · Electrical Resistivity 5.7×10⁻⁷ Ω·m22.4 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 75%
Common Calculations
Ratios derived from the values above.
Modulus of Resilience
Thermal Diffusivity
Same in both: Specific Strength (UTS / density) 100 kN·m/kg · Specific Stiffness (E / density) 26.3 MN·m/kg · Thermal Shock Resistance Index 9
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1.4011 | CA40F |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 7 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Pickling, Plasma Spray, Silver Plating.
1.4011 vs CA40F — frequently asked
What is the difference between 1.4011 and CA40F?
Stainless Steel 1.4011 and CA40F are both stainless steel grades. Both yield at about 550 MPa — strength does not separate them. 1.4011 is the more ductile: elongation 22% versus 14% for CA40F, and CA40F is harder (240 HB vs 225 HB).
Which is cheaper, 1.4011 or CA40F?
Both sit in the same relative cost tier ($$$, premium); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 1.4011 or CA40F?
CA40F. Its machinability rates good (58/100) against fair (45/100) for 1.4011; for welding the order is 1.4011 first (fair, 40/100) then CA40F (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1.4011 and CA40F side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.