Solder & Low-Melting Alloy Sn60Pb40Sb vs Sn95Cu4Ag1
Solder & Low-Melting Alloy · grade comparison
Solder & Low-Melting Alloy Sn60Pb40Sb and Sn95Cu4Ag1 are both solder & low-melting alloy grades. Sn60Pb40Sb is the stronger of the two: tensile strength 52 MPa (7.54 ksi) against 48 MPa (6.96 ksi) for Sn95Cu4Ag1, about 8% more. Sn60Pb40Sb is the more ductile: elongation 35% versus 25% for Sn95Cu4Ag1, and Sn95Cu4Ag1 is harder (18 HB vs 15 HB). Sn95Cu4Ag1 is lighter (7.35 g/cm³ vs 8.5 g/cm³ for Sn60Pb40Sb) and Sn95Cu4Ag1 is stiffer (48 GPa vs 31 GPa). On the shop floor, Sn95Cu4Ag1 welds better (poor vs not recommended).
Sn60Pb40SbChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
Sn95Cu4Ag1Choose it when weight is the constraint, or when the part sees heat.
Sn60Pb40Sb vs Sn95Cu4Ag1: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all solder & low-melting alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all solder & low-melting alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Compressive Strength
Same in both: Yield Strength (0.2% offset) 32 MPa4.6 ksi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -55°C-67 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 11.5 % IACS · Electrical Resistivity 1.5×10⁻⁷ Ω·m5.91 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.5 V · Corrosion Resistance 45 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Same in both: Polishability 25 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 3
Strength versus weight
Yield strength against density for every solder & low-melting alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Sn60Pb40Sb | Sn95Cu4Ag1 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Sn60Pb40Sb vs Sn95Cu4Ag1 — frequently asked
Is Sn60Pb40Sb stronger than Sn95Cu4Ag1?
Yes. Sn60Pb40Sb has a typical tensile strength of 52 MPa (7.54 ksi) against 48 MPa (6.96 ksi) for Sn95Cu4Ag1 — about 8% more.
Which is cheaper, Sn60Pb40Sb or Sn95Cu4Ag1?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, Sn60Pb40Sb or Sn95Cu4Ag1?
Sn60Pb40Sb. Its machinability rates fair (35/100) against poor (30/100) for Sn95Cu4Ag1; for welding the order is Sn95Cu4Ag1 first (poor, 20/100) then Sn60Pb40Sb (not recommended, 10/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Sn60Pb40Sb and Sn95Cu4Ag1 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.