Solder & Low-Melting Alloy Sn40Pb60 vs Sn60Pb40Sb
Solder & Low-Melting Alloy · grade comparison
Solder & Low-Melting Alloy Sn40Pb60 and Sn60Pb40Sb are both solder & low-melting alloy grades. Sn60Pb40Sb is the stronger of the two: yield strength 32 MPa (4.64 ksi) against 22 MPa (3.19 ksi) for Sn40Pb60, about 45% more; tensile strength follows at 52 MPa (7.54 ksi) vs 38 MPa (5.51 ksi). In exchange, Sn40Pb60 is the more ductile: elongation 55% versus 35% for Sn60Pb40Sb, and Sn60Pb40Sb is harder (15 HB vs 12 HB). Sn60Pb40Sb is lighter (8.5 g/cm³ vs 9.29 g/cm³ for Sn40Pb60) and Sn60Pb40Sb is stiffer (31 GPa vs 25 GPa).
Sn40Pb60Choose it when the part is bent, formed or impact-loaded.
Sn60Pb40SbChoose it when strength drives the design, or when weight is the constraint.
Sn40Pb60 vs Sn60Pb40Sb: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all solder & low-melting alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all solder & low-melting alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Charpy V-Notch Impact (RT)
Same in both: Bulk Modulus 42 GPa6.1 Msi
Physical
Density and transition temperatures.
Density
Liquidus Temperature
Same in both: Melting Point (Solidus) 183°C361 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 176 J/kg·K0.04 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 24.5 µm/m·K13.6 µin/in·°F · Min Service Temperature -55°C-67 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 45 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Formability (cold)
Brazeability / Solderability
Polishability
Weldability
Same in both: Machinability 35 / 100 · Castability 95 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 3
Strength versus weight
Yield strength against density for every solder & low-melting alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Sn40Pb60 | Sn60Pb40Sb |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Sn40Pb60 vs Sn60Pb40Sb — frequently asked
Is Sn60Pb40Sb stronger than Sn40Pb60?
Yes. Sn60Pb40Sb has a typical yield strength of 32 MPa (4.64 ksi) against 22 MPa (3.19 ksi) for Sn40Pb60 — about 45% more. Tensile strength is 52 MPa (7.54 ksi) vs 38 MPa (5.51 ksi).
Which is cheaper, Sn40Pb60 or Sn60Pb40Sb?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose Sn40Pb60 over Sn60Pb40Sb?
Pick Sn40Pb60 when the part is bent, formed or impact-loaded. Pick Sn60Pb40Sb when strength drives the design, or when weight is the constraint.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Sn40Pb60 and Sn60Pb40Sb side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.