Solder & Low-Melting Alloy Pb50Sn50 vs Pb98Sn2
Solder & Low-Melting Alloy · grade comparison
Solder & Low-Melting Alloy Pb50Sn50 and Pb98Sn2 are both solder & low-melting alloy grades. Pb50Sn50 is the stronger of the two: yield strength 27 MPa (3.92 ksi) against 9 MPa (1.31 ksi) for Pb98Sn2, about 3.0 times as much; tensile strength follows at 42 MPa (6.09 ksi) vs 19 MPa (2.76 ksi). Pb50Sn50 is the more ductile: elongation 55% versus 45% for Pb98Sn2, and Pb50Sn50 is harder (14 HB vs 6 HB). Pb50Sn50 is lighter (8.85 g/cm³ vs 11.2 g/cm³ for Pb98Sn2) and Pb50Sn50 is stiffer (23 GPa vs 16 GPa). On the shop floor, Pb98Sn2 machines more easily (fair vs poor) and Pb98Sn2 sits in a lower cost tier (premium, $$$) than Pb50Sn50 (high, $$$$).
Pb50Sn50Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
Pb98Sn2Choose it when the part sees heat, or when the part is machined in volume.
Pb50Sn50 vs Pb98Sn2: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all solder & low-melting alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all solder & low-melting alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 45 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Brazeability / Solderability
Same in both: Formability (cold) 95 / 100 · Castability 90 / 100 · Polishability 20 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every solder & low-melting alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Pb50Sn50 | Pb98Sn2 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Pb50Sn50 vs Pb98Sn2 — frequently asked
Is Pb50Sn50 stronger than Pb98Sn2?
Yes. Pb50Sn50 has a typical yield strength of 27 MPa (3.92 ksi) against 9 MPa (1.31 ksi) for Pb98Sn2 — about 3.0 times as much. Tensile strength is 42 MPa (6.09 ksi) vs 19 MPa (2.76 ksi).
Which is cheaper, Pb50Sn50 or Pb98Sn2?
Pb98Sn2 is the lower-cost material: it sits in the premium tier ($$$) while Pb50Sn50 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, Pb50Sn50 or Pb98Sn2?
Pb98Sn2. Its machinability rates fair (40/100) against poor (30/100) for Pb50Sn50; for welding the order is Pb98Sn2 first (poor, 20/100) then Pb50Sn50 (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Pb50Sn50 and Pb98Sn2 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.