Precious Metal AgCu-Eutectic-H02 vs AgCu-Eutectic-O
Precious Metal · AgCu-Eutectic temper comparison
AgCu-Eutectic-H02 and AgCu-Eutectic-O are two conditions of the same precious metal grade, AgCu-Eutectic: H02 (half hard) versus O (annealed). The chemistry is identical, so every difference below comes from the condition. AgCu-Eutectic-H02 is the stronger of the two: yield strength 330 MPa (47.9 ksi) against 130 MPa (18.9 ksi) for AgCu-Eutectic-O, about 154% more; tensile strength follows at 420 MPa (60.9 ksi) vs 300 MPa (43.5 ksi). In exchange, AgCu-Eutectic-O is the more ductile: elongation 30% versus 10% for AgCu-Eutectic-H02, and AgCu-Eutectic-H02 is harder (105 HB vs 65 HB). AgCu-Eutectic-O runs hotter in service (300°C vs 180°C continuous). On the shop floor, AgCu-Eutectic-H02 machines more easily (good vs fair).
AgCu-Eutectic-H02Choose it when strength drives the design, or when the part is machined in volume.
AgCu-Eutectic-OChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
AgCu-Eutectic-H02 vs AgCu-Eutectic-O: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
AgCu-Eutectic-H02AgCu-Eutectic-O
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 85 GPa12.3 Msi · Shear Modulus 32 GPa4.6 Msi · Bulk Modulus 108 GPa15.7 Msi · Poisson's Ratio 0.36
Physical
Density and transition temperatures.
Same in both: Density 9.9 g/cm³0.36 lb/in³ · Melting Point (Solidus) 779°C1,434 °F · Liquidus Temperature 780°C1,436 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 275 J/kg·K0.07 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 19 µm/m·K10.6 µin/in·°F · Latent Heat of Fusion 140 J/g60.2 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V · Corrosion Resistance 75 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 85 / 100 · Brazeability / Solderability 98 / 100 · Polishability 88 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 1,130 MJ/kg485,813 BTU/lb · Embodied Carbon (primary production) 80 kg CO₂/kg · Embodied Water 90,000 L/kg10,784 gal/lb · Typical Recycled Content 45%
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
AgCu-Eutectic-H02 vs AgCu-Eutectic-O — frequently asked
Is AgCu-Eutectic-H02 stronger than AgCu-Eutectic-O?
Yes. AgCu-Eutectic-H02 has a typical yield strength of 330 MPa (47.9 ksi) against 130 MPa (18.9 ksi) for AgCu-Eutectic-O — about 154% more. Tensile strength is 420 MPa (60.9 ksi) vs 300 MPa (43.5 ksi).
Which condition does FabDigit quote by default, H02 or O?
O is the default AgCu-Eutectic condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, AgCu-Eutectic-H02 or AgCu-Eutectic-O?
AgCu-Eutectic-H02. Its machinability rates good (60/100) against fair (50/100) for AgCu-Eutectic-O.