Precious Metal AgCu-Eutectic-AB vs AgCu-Eutectic-O
Precious Metal · AgCu-Eutectic temper comparison
AgCu-Eutectic-AB and AgCu-Eutectic-O are two conditions of the same precious metal grade, AgCu-Eutectic: AB (as built (as printed)) versus O (annealed). The chemistry is identical, so every difference below comes from the condition. AgCu-Eutectic-AB is the stronger of the two: yield strength 150 MPa (21.8 ksi) against 130 MPa (18.9 ksi) for AgCu-Eutectic-O, about 15% more. In exchange, AgCu-Eutectic-O is the more ductile: elongation 30% versus 18% for AgCu-Eutectic-AB, and AgCu-Eutectic-O is harder (65 HB vs 60 HB).
AgCu-Eutectic-ABChoose it when strength drives the design.
AgCu-Eutectic-OChoose it when the part is bent, formed or impact-loaded.
AgCu-Eutectic-AB vs AgCu-Eutectic-O: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
AgCu-Eutectic-ABAgCu-Eutectic-O
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 32 GPa4.6 Msi · Bulk Modulus 108 GPa15.7 Msi · Poisson's Ratio 0.36
Physical
Density and transition temperatures.
Same in both: Density 9.9 g/cm³0.36 lb/in³ · Melting Point (Solidus) 779°C1,434 °F · Liquidus Temperature 780°C1,436 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 275 J/kg·K0.07 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 19 µm/m·K10.6 µin/in·°F · Latent Heat of Fusion 140 J/g60.2 BTU/lb · Max Service Temperature (continuous) 300°C572 °F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Formability (cold)
Same in both: Machinability 50 / 100 · Machinability Rating (AISI 1212 = 100 %) 50% · Castability 85 / 100 · Brazeability / Solderability 98 / 100 · Polishability 88 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 1,130 MJ/kg485,813 BTU/lb · Embodied Carbon (primary production) 80 kg CO₂/kg · Embodied Water 90,000 L/kg10,784 gal/lb · Typical Recycled Content 45%
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
AgCu-Eutectic-AB vs AgCu-Eutectic-O — frequently asked
Is AgCu-Eutectic-AB stronger than AgCu-Eutectic-O?
Yes. AgCu-Eutectic-AB has a typical yield strength of 150 MPa (21.8 ksi) against 130 MPa (18.9 ksi) for AgCu-Eutectic-O — about 15% more. Tensile strength is 275 MPa (39.9 ksi) vs 300 MPa (43.5 ksi).
Which condition does FabDigit quote by default, AB or O?
O is the default AgCu-Eutectic condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, AgCu-Eutectic-AB or AgCu-Eutectic-O?
AgCu-Eutectic-O. Its weldability rates fair (40/100) against fair (35/100) for AgCu-Eutectic-AB.
Ready to make it?
Upload a CAD file and FabDigit prices the part in AgCu-Eutectic-AB and AgCu-Eutectic-O side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.