Precious Metal AgCu-Eutectic-H02 vs AgCu-Eutectic-H04
Precious Metal · AgCu-Eutectic temper comparison
AgCu-Eutectic-H02 and AgCu-Eutectic-H04 are two conditions of the same precious metal grade, AgCu-Eutectic: H02 (half hard) versus H04 (full hard). The chemistry is identical, so every difference below comes from the condition. AgCu-Eutectic-H04 is the stronger of the two: yield strength 480 MPa (69.6 ksi) against 330 MPa (47.9 ksi) for AgCu-Eutectic-H02, about 45% more; tensile strength follows at 550 MPa (79.8 ksi) vs 420 MPa (60.9 ksi). In exchange, AgCu-Eutectic-H02 is the more ductile: elongation 10% versus 3% for AgCu-Eutectic-H04, and AgCu-Eutectic-H04 is harder (138 HB vs 105 HB). AgCu-Eutectic-H04 runs hotter in service (300°C vs 180°C continuous).
AgCu-Eutectic-H02Choose it when the part is bent, formed or impact-loaded.
AgCu-Eutectic-H04Choose it when strength drives the design, or when the part sees heat.
AgCu-Eutectic-H02 vs AgCu-Eutectic-H04: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
AgCu-Eutectic-H02AgCu-Eutectic-H04
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 85 GPa12.3 Msi · Shear Modulus 32 GPa4.6 Msi · Bulk Modulus 108 GPa15.7 Msi · Poisson's Ratio 0.36
Physical
Density and transition temperatures.
Same in both: Density 9.9 g/cm³0.36 lb/in³ · Melting Point (Solidus) 779°C1,434 °F · Liquidus Temperature 780°C1,436 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 275 J/kg·K0.07 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 19 µm/m·K10.6 µin/in·°F · Latent Heat of Fusion 140 J/g60.2 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V · Corrosion Resistance 75 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 85 / 100 · Brazeability / Solderability 98 / 100 · Polishability 88 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 1,130 MJ/kg485,813 BTU/lb · Embodied Carbon (primary production) 80 kg CO₂/kg · Embodied Water 90,000 L/kg10,784 gal/lb · Typical Recycled Content 45%
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
AgCu-Eutectic-H02 vs AgCu-Eutectic-H04 — frequently asked
Is AgCu-Eutectic-H04 stronger than AgCu-Eutectic-H02?
Yes. AgCu-Eutectic-H04 has a typical yield strength of 480 MPa (69.6 ksi) against 330 MPa (47.9 ksi) for AgCu-Eutectic-H02 — about 45% more. Tensile strength is 550 MPa (79.8 ksi) vs 420 MPa (60.9 ksi).
Which condition does FabDigit quote by default, H02 or H04?
O is the default AgCu-Eutectic condition in the FabDigit quote flow (neither H02 nor H04). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, AgCu-Eutectic-H02 or AgCu-Eutectic-H04?
AgCu-Eutectic-H04, by a small margin. Both rate good for machinability — 65/100 against 60/100 for AgCu-Eutectic-H02.
Ready to make it?
Upload a CAD file and FabDigit prices the part in AgCu-Eutectic-H02 and AgCu-Eutectic-H04 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.