Precious Metal 92Ag-8SnO2-H02 vs 92Ag-8SnO2-H04
Precious Metal · 92Ag-8SnO2 temper comparison
92Ag-8SnO2-H02 and 92Ag-8SnO2-H04 are two conditions of the same precious metal grade, 92Ag-8SnO2: H02 (half hard) versus H04 (full hard). The chemistry is identical, so every difference below comes from the condition. 92Ag-8SnO2-H04 is the stronger of the two: yield strength 275 MPa (39.9 ksi) against 200 MPa (29 ksi) for 92Ag-8SnO2-H02, about 38% more; tensile strength follows at 325 MPa (47.1 ksi) vs 275 MPa (39.9 ksi). In exchange, 92Ag-8SnO2-H02 is the more ductile: elongation 8% versus 4% for 92Ag-8SnO2-H04, and 92Ag-8SnO2-H04 is harder (90 HB vs 74 HB). 92Ag-8SnO2-H02 runs hotter in service (180°C vs 150°C continuous).
92Ag-8SnO2-H02Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
92Ag-8SnO2-H04Choose it when strength drives the design.
92Ag-8SnO2-H02 vs 92Ag-8SnO2-H04: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 88 GPa12.8 Msi · Shear Modulus 32 GPa4.6 Msi · Bulk Modulus 105 GPa15.2 Msi · Poisson's Ratio 0.37
Physical
Density and transition temperatures.
Same in both: Density 10.1 g/cm³0.36 lb/in³ · Melting Point (Solidus) 961°C1,762 °F · Liquidus Temperature 961°C1,762 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 240 J/kg·K0.06 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 19 µm/m·K10.6 µin/in·°F · Latent Heat of Fusion 100 J/g43 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) 0.05 V · Corrosion Resistance 88 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 85 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 1,450 MJ/kg623,388 BTU/lb · Embodied Carbon (primary production) 110 kg CO₂/kg · Embodied Water 2,000 L/kg240 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
92Ag-8SnO2-H02 vs 92Ag-8SnO2-H04 — frequently asked
Is 92Ag-8SnO2-H04 stronger than 92Ag-8SnO2-H02?
Yes. 92Ag-8SnO2-H04 has a typical yield strength of 275 MPa (39.9 ksi) against 200 MPa (29 ksi) for 92Ag-8SnO2-H02 — about 38% more. Tensile strength is 325 MPa (47.1 ksi) vs 275 MPa (39.9 ksi).
Which condition does FabDigit quote by default, H02 or H04?
O is the default 92Ag-8SnO2 condition in the FabDigit quote flow (neither H02 nor H04). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 92Ag-8SnO2-H02 or 92Ag-8SnO2-H04?
92Ag-8SnO2-H04. Its machinability rates good (55/100) against fair (48/100) for 92Ag-8SnO2-H02.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 92Ag-8SnO2-H02 and 92Ag-8SnO2-H04 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.