Precious Metal 80Ag-20CdO vs AgC10
Precious Metal · grade comparison
Precious Metal 80Ag-20CdO and AgC10 are both precious metal grades. 80Ag-20CdO is the stronger of the two: yield strength 135 MPa (19.6 ksi) against 70 MPa (10.2 ksi) for AgC10, about 93% more; tensile strength follows at 265 MPa (38.4 ksi) vs 110 MPa (16 ksi). 80Ag-20CdO is the more ductile: elongation 15% versus 4% for AgC10, and 80Ag-20CdO is harder (66 HB vs 30 HB). AgC10 is lighter (7.6 g/cm³ vs 9.9 g/cm³ for 80Ag-20CdO) and 80Ag-20CdO is stiffer (85 GPa vs 55 GPa). On the shop floor, AgC10 machines more easily (good vs fair) and 80Ag-20CdO welds better (fair vs poor).
80Ag-20CdOChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
AgC10Choose it when weight is the constraint, or when the part sees heat.
80Ag-20CdO vs AgC10: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Compressive Strength
Physical
Density and transition temperatures.
Density
Same in both: Melting Point (Solidus) 961°C1,762 °F · Liquidus Temperature 961°C1,762 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -60°C-76 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) 0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 80Ag-20CdO | AgC10 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
80Ag-20CdO vs AgC10 — frequently asked
Is 80Ag-20CdO stronger than AgC10?
Yes. 80Ag-20CdO has a typical yield strength of 135 MPa (19.6 ksi) against 70 MPa (10.2 ksi) for AgC10 — about 93% more. Tensile strength is 265 MPa (38.4 ksi) vs 110 MPa (16 ksi).
Which is cheaper, 80Ag-20CdO or AgC10?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 80Ag-20CdO or AgC10?
AgC10. Its machinability rates good (55/100) against fair (45/100) for 80Ag-20CdO; for welding the order is 80Ag-20CdO first (fair, 35/100) then AgC10 (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 80Ag-20CdO and AgC10 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.