Precious Metal 22K vs 24K
Precious Metal · grade comparison
Precious Metal 22K and 24K are both precious metal grades. 22K is the stronger of the two: yield strength 75 MPa (10.9 ksi) against 30 MPa (4.35 ksi) for 24K, about 150% more; tensile strength follows at 220 MPa (31.9 ksi) vs 125 MPa (18.1 ksi). In exchange, 24K is the more ductile: elongation 45% versus 35% for 22K, and 22K is harder (52 HB vs 25 HB). 22K is lighter (17.8 g/cm³ vs 19.32 g/cm³ for 24K) and 24K runs hotter in service (600°C vs 400°C continuous). On the shop floor, 22K machines more easily (fair vs poor).
22KChoose it when strength drives the design, or when weight is the constraint.
24KChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
22K vs 24K: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 78 GPa11.3 Msi · Poisson's Ratio 0.42
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) 0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Castability 85 / 100 · Brazeability / Solderability 95 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 150,000 L/kg17,974 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 22K | 24K |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
22K vs 24K — frequently asked
Is 22K stronger than 24K?
Yes. 22K has a typical yield strength of 75 MPa (10.9 ksi) against 30 MPa (4.35 ksi) for 24K — about 150% more. Tensile strength is 220 MPa (31.9 ksi) vs 125 MPa (18.1 ksi).
Which is cheaper, 22K or 24K?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 22K or 24K?
22K. Its machinability rates fair (50/100) against poor (30/100) for 24K; for welding the order is 24K first (excellent, 90/100) then 22K (excellent, 85/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 22K and 24K side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.