Precious Metal 10K vs 18K Rose Gold
Precious Metal · grade comparison
Precious Metal 10K and 18K Rose Gold are both precious metal grades. 18K Rose Gold is the stronger of the two: yield strength 210 MPa (30.5 ksi) against 190 MPa (27.6 ksi) for 10K, about 11% more; tensile strength follows at 460 MPa (66.7 ksi) vs 420 MPa (60.9 ksi). 18K Rose Gold is harder — 143 HB against 118 HB for 10K — which matters for wear surfaces and threads. 10K is lighter (11.55 g/cm³ vs 15.3 g/cm³ for 18K Rose Gold) and 10K is stiffer (96 GPa vs 88 GPa). On the shop floor, 10K welds better (very good vs good).
10KChoose it when weight is the constraint, or when it will be welded.
18K Rose GoldChoose it when strength drives the design, or when surface hardness matters.
10K vs 18K Rose Gold: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Reduction in Area
Charpy V-Notch Impact (RT)
Hardness, Rockwell B
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Latent Heat of Fusion
Min Service Temperature
Same in both: Thermal Expansion (CTE, 20–100 °C) 16 µm/m·K8.9 µin/in·°F · Max Service Temperature (continuous) 300°C572 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) 0.2 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Castability
Brazeability / Solderability
Polishability
Machinability Rating (AISI 1212 = 100 %)
Same in both: Formability (cold) 85 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 10K | 18K Rose Gold |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
10K vs 18K Rose Gold — frequently asked
Is 18K Rose Gold stronger than 10K?
Yes. 18K Rose Gold has a typical yield strength of 210 MPa (30.5 ksi) against 190 MPa (27.6 ksi) for 10K — about 11% more. Tensile strength is 460 MPa (66.7 ksi) vs 420 MPa (60.9 ksi).
Which is cheaper, 10K or 18K Rose Gold?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 10K or 18K Rose Gold?
18K Rose Gold. Its machinability rates good (58/100) against fair (50/100) for 10K; for welding the order is 10K first (very good, 75/100) then 18K Rose Gold (good, 62/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 10K and 18K Rose Gold side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.