PBI vs Vinyl Ester
Polymer · grade comparison
PBI and Vinyl Ester are both polymer grades. PBI is the stronger of the two: tensile strength 160 MPa (23.2 ksi) against 84 MPa (12.2 ksi) for Vinyl Ester, about 90% more. In exchange, Vinyl Ester is the more ductile: elongation 5.5% versus 3% for PBI. Vinyl Ester is lighter (1.13 g/cm³ vs 1.3 g/cm³ for PBI) and PBI is stiffer (5.9 GPa vs 3.3 GPa). On the shop floor, Vinyl Ester sits in a lower cost tier (standard, $$) than PBI (specialty, $$$$$).
PBIChoose it when strength drives the design, or when the part sees heat.
Vinyl EsterChoose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
PBI vs Vinyl Ester: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Compressive Modulus
Flexural Strength
Flexural Modulus
Shear Strength
Izod Impact, Notched
Hardness, Rockwell M
Shear Modulus
Bulk Modulus
Fracture Toughness (K_IC)
Hardness, Shore D
Physical
Density and transition temperatures.
Density
Glass Transition (Tg)
Water Absorption (24 h)
Water Absorption (Saturation)
Refractive Index
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Heat Deflection Temp. @ 1.8 MPa
Limiting Oxygen Index
Max Service Temperature (short-term)
Heat Deflection Temp. @ 0.45 MPa
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Strength
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Volume Resistivity
Surface Resistivity
Comparative Tracking Index (CTI)
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Mold Shrinkage
Mold Temperature (typ.)
Same in both: Weldability 5 / 100 · Formability (cold) 5 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 0%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | PBI | Vinyl Ester |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Injection molding | Yes | — |
| Default condition | Unfilled | — |
| Relative cost | $$$$$ Specialty | $$ Standard |
| Min. machined wall | 0.5 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| Chrome Plating (Plastic) | Yes | — |
| EMI Shielding Coating | Yes | — |
| Painting | Yes | — |
| Soft Touch Coating | Yes | — |
| Spray Painting | Yes | — |
| UV Coating | Yes | — |
PBI vs Vinyl Ester — frequently asked
Is PBI stronger than Vinyl Ester?
Yes. PBI has a typical tensile strength of 160 MPa (23.2 ksi) against 84 MPa (12.2 ksi) for Vinyl Ester — about 90% more.
Which is cheaper, PBI or Vinyl Ester?
Vinyl Ester is the lower-cost material: it sits in the standard tier ($$) while PBI is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, PBI or Vinyl Ester?
Vinyl Ester. Its machinability rates good (55/100) against fair (50/100) for PBI.
Ready to make it?
Upload a CAD file and FabDigit prices the part in PBI and Vinyl Ester side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.