LCP Type I vs Sumikasuper
Polymer · grade comparison
LCP Type I and Sumikasuper are both polymer grades. Sumikasuper is the stronger of the two: tensile strength 160 MPa (23.2 ksi) against 135 MPa (19.6 ksi) for LCP Type I, about 19% more. In exchange, LCP Type I is the more ductile: elongation 2.5% versus 2.2% for Sumikasuper. LCP Type I is lighter (1.38 g/cm³ vs 1.62 g/cm³ for Sumikasuper) and Sumikasuper is stiffer (14 GPa vs 11 GPa). On the shop floor, LCP Type I machines more easily (good vs fair) and Sumikasuper welds better (30 vs 20 out of 100).
LCP Type IChoose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
SumikasuperChoose it when strength drives the design, or when it will be welded.
LCP Type I vs Sumikasuper: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Compressive Modulus
Flexural Strength
Flexural Modulus
Shear Strength
Izod Impact, Notched
Hardness, Rockwell M
Same in both: Hardness, Shore D 88 Shore D
Physical
Density and transition temperatures.
Density
Melting Temperature (Tm)
Glass Transition (Tg)
Water Absorption (Saturation)
Same in both: Water Absorption (24 h) 0.02%
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Min Service Temperature
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Same in both: Thermal Expansion (CTE, 20–100 °C) 8 µm/m·K4.4 µin/in·°F · Max Service Temperature (continuous) 220°C428 °F · Limiting Oxygen Index 40% · Max Service Temperature (short-term) 300°C572 °F
Electrical
Conductivity and insulation.
Dielectric Strength
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Same in both: Electrical Resistivity 1×10¹³ Ω·m3.94×10²⁰ µΩ·in · Volume Resistivity 1×10¹⁵ Ω·cm · Surface Resistivity 1×10¹⁵ Ω · Comparative Tracking Index (CTI) 200 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Polishability
Mold Shrinkage
Processing Melt Temperature (typ.)
Mold Temperature (typ.)
Melt Flow Rate
Same in both: Formability (cold) 20 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Same in both: Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 0%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | LCP Type I | Sumikasuper |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
LCP Type I vs Sumikasuper — frequently asked
Is Sumikasuper stronger than LCP Type I?
Yes. Sumikasuper has a typical tensile strength of 160 MPa (23.2 ksi) against 135 MPa (19.6 ksi) for LCP Type I — about 19% more.
Which is cheaper, LCP Type I or Sumikasuper?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, LCP Type I or Sumikasuper?
LCP Type I. Its machinability rates good (62/100) against fair (45/100) for Sumikasuper; for welding the order is Sumikasuper first (poor, 30/100) then LCP Type I (poor, 20/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in LCP Type I and Sumikasuper side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.