ABS vs GPPS
Polymer · grade comparison
ABS and GPPS are both polymer grades. GPPS is the stronger of the two: tensile strength 46 MPa (6.67 ksi) against 43 MPa (6.24 ksi) for ABS, about 7% more. In exchange, ABS is the more ductile: elongation 25% versus 2.5% for GPPS, and GPPS is harder (85 Shore D vs 78 Shore D). GPPS is stiffer (3.2 GPa vs 2.3 GPa) and ABS runs hotter in service (75°C vs 65°C continuous). On the shop floor, ABS machines more easily (very good vs good).
ABSChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
GPPSChoose it when strength drives the design.
ABS vs GPPS: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Compressive Modulus
Flexural Strength
Flexural Modulus
Shear Strength
Fracture Toughness (K_IC)
Izod Impact, Notched
Hardness, Shore D
Hardness, Rockwell R
Hardness, Rockwell M
Physical
Density and transition temperatures.
Density
Glass Transition (Tg)
Water Absorption (24 h)
Water Absorption (Saturation)
Refractive Index
Light Transmission
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Vicat Softening Point (B50)
Limiting Oxygen Index
Max Service Temperature (short-term)
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Strength
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Volume Resistivity
Same in both: Surface Resistivity 1×10¹⁵ Ω · Comparative Tracking Index (CTI) 600 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Polishability
Mold Shrinkage
Melt Flow Rate
Processing Melt Temperature (typ.)
Mold Temperature (typ.)
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Same in both: Thermal Diffusivity 0.1 mm²/s · Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | ABS | GPPS |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Injection molding | Yes | — |
| 3D printing | Yes | — |
| Default condition | Unfilled | — |
| Relative cost | $ Budget | $ Budget |
| Min. machined wall | 0.5 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| Chrome Plating (Plastic) | Yes | — |
| Conductive Coating | Yes | — |
| Dyeing (Nylon) | Yes | — |
| EMI Shielding Coating | Yes | — |
| Painting | Yes | — |
| Primer Coating | Yes | — |
| Soft Touch Coating | Yes | — |
| Spray Painting | Yes | — |
| Tinted Coating | Yes | — |
| UV Coating | Yes | — |
| Vacuum Metallization | Yes | — |
| Waterproof Coating | Yes | — |
ABS vs GPPS — frequently asked
Is GPPS stronger than ABS?
Yes. GPPS has a typical tensile strength of 46 MPa (6.67 ksi) against 43 MPa (6.24 ksi) for ABS — about 7% more.
Which is cheaper, ABS or GPPS?
Both sit in the same relative cost tier ($, budget); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, ABS or GPPS?
ABS. Its machinability rates very good (80/100) against good (55/100) for GPPS.