Nickel Alloy N06110-CD vs N06110 HF-A
Nickel Alloy · N06110 temper comparison
N06110-CD and N06110 HF-A are two conditions of the same nickel alloy grade, N06110: CD (cold drawn) versus HF-A (hot Finished + Annealed). The chemistry is identical, so every difference below comes from the condition. N06110-CD is the stronger of the two: yield strength 830 MPa (120 ksi) against 370 MPa (53.7 ksi) for N06110 HF-A, about 124% more; tensile strength follows at 1,000 MPa (145 ksi) vs 770 MPa (112 ksi). In exchange, N06110 HF-A is the more ductile: elongation 48% versus 22% for N06110-CD, and N06110-CD is harder (300 HB vs 195 HB). N06110 HF-A runs hotter in service (650°C vs 540°C continuous). On the shop floor, N06110 HF-A welds better (very good vs good).
N06110-CDChoose it when strength drives the design.
N06110 HF-AChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
N06110-CD vs N06110 HF-A: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 175 GPa25.4 Msi · Poisson's Ratio 0.31
Physical
Density and transition temperatures.
Same in both: Density 8.4 g/cm³0.3 lb/in³ · Melting Point (Solidus) 1,330°C2,426 °F · Liquidus Temperature 1,380°C2,516 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 9 W/m·K5.2 BTU/hr·ft·°F · Specific Heat Capacity 430 J/kg·K0.1 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.3 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 290 J/g125 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 1.4 % IACS · Electrical Resistivity 1.25×10⁻⁶ Ω·m49.2 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 35 / 100 · Brazeability / Solderability 55 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 150 MJ/kg64,488 BTU/lb · Embodied Carbon (primary production) 13 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
N06110-CD vs N06110 HF-A — frequently asked
Is N06110-CD stronger than N06110 HF-A?
Yes. N06110-CD has a typical yield strength of 830 MPa (120 ksi) against 370 MPa (53.7 ksi) for N06110 HF-A — about 124% more. Tensile strength is 1,000 MPa (145 ksi) vs 770 MPa (112 ksi).
Which condition does FabDigit quote by default, CD or HF-A?
SA is the default N06110 condition in the FabDigit quote flow (neither CD nor HF-A). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, N06110-CD or N06110 HF-A?
N06110 HF-A. Its weldability rates very good (70/100) against good (60/100) for N06110-CD.
Ready to make it?
Upload a CAD file and FabDigit prices the part in N06110-CD and N06110 HF-A side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.