Nickel Alloy Alloy 45TM vs Inconel 600
Nickel Alloy · grade comparison
Nickel Alloy Alloy 45TM and Inconel 600 are both nickel alloy grades. Alloy 45TM is the stronger of the two: yield strength 330 MPa (47.9 ksi) against 255 MPa (37 ksi) for Inconel 600, about 29% more; tensile strength follows at 730 MPa (106 ksi) vs 620 MPa (89.9 ksi). Alloy 45TM is harder — 180 HB against 150 HB for Inconel 600 — which matters for wear surfaces and threads. Alloy 45TM is lighter (7.6 g/cm³ vs 8.47 g/cm³ for Inconel 600) and Inconel 600 is stiffer (214 GPa vs 195 GPa). On the shop floor, Inconel 600 welds better (very good vs good) and Inconel 600 forms better (very good vs good).
Alloy 45TMChoose it when strength drives the design, or when surface hardness matters.
Inconel 600Choose it when it will be welded.
Alloy 45TM vs Inconel 600: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Reduction in Area
Compressive Strength
Shear Strength
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Fracture Toughness (K_IC)
Same in both: Elongation at Break 42% · Fatigue Strength (Endurance Limit) 280 MPa40.6 ksi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Min Service Temperature
Latent Heat of Fusion
Same in both: Max Service Temperature (continuous) 1,100°C2,012 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Castability
Sustainability
Primary-production footprint per kilogram.
Embodied Water
Same in both: Embodied Energy (primary production) 150 MJ/kg64,488 BTU/lb · Embodied Carbon (primary production) 11.5 kg CO₂/kg · Typical Recycled Content 40%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 3
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Alloy 45TM | Inconel 600 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 3 finishes: Gold Plating, Plasma Spray, Silver Plating.
Alloy 45TM vs Inconel 600 — frequently asked
Is Alloy 45TM stronger than Inconel 600?
Yes. Alloy 45TM has a typical yield strength of 330 MPa (47.9 ksi) against 255 MPa (37 ksi) for Inconel 600 — about 29% more. Tensile strength is 730 MPa (106 ksi) vs 620 MPa (89.9 ksi).
Which is cheaper, Alloy 45TM or Inconel 600?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which welds better, Alloy 45TM or Inconel 600?
Inconel 600. Its weldability rates very good (80/100) against good (60/100) for Alloy 45TM.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Alloy 45TM and Inconel 600 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.