Nickel Alloy ENiCrCoMo-1 vs ENiCu-7
Nickel Alloy · grade comparison
Nickel Alloy ENiCrCoMo-1 and ENiCu-7 are both nickel alloy grades. ENiCrCoMo-1 is the stronger of the two: yield strength 430 MPa (62.4 ksi) against 290 MPa (42.1 ksi) for ENiCu-7, about 48% more; tensile strength follows at 720 MPa (104 ksi) vs 520 MPa (75.4 ksi). ENiCrCoMo-1 is harder — 210 HB against 165 HB for ENiCu-7 — which matters for wear surfaces and threads. ENiCrCoMo-1 is lighter (8.36 g/cm³ vs 8.83 g/cm³ for ENiCu-7) and ENiCrCoMo-1 is stiffer (211 GPa vs 179 GPa). On the shop floor, ENiCu-7 machines more easily (30 vs 20 out of 100) and ENiCrCoMo-1 welds better (excellent vs very good).
ENiCrCoMo-1Choose it when strength drives the design, or when surface hardness matters.
ENiCu-7Choose it when the part is machined in volume.
ENiCrCoMo-1 vs ENiCu-7: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Rockwell C
Hardness, Vickers
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Latent Heat of Fusion 290 J/g125 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Brazeability / Solderability
Same in both: Formability (cold) 35 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 30%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | ENiCrCoMo-1 | ENiCu-7 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 3 finishes: Gold Plating, Plasma Spray, Silver Plating.
ENiCrCoMo-1 vs ENiCu-7 — frequently asked
Is ENiCrCoMo-1 stronger than ENiCu-7?
Yes. ENiCrCoMo-1 has a typical yield strength of 430 MPa (62.4 ksi) against 290 MPa (42.1 ksi) for ENiCu-7 — about 48% more. Tensile strength is 720 MPa (104 ksi) vs 520 MPa (75.4 ksi).
Which is cheaper, ENiCrCoMo-1 or ENiCu-7?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, ENiCrCoMo-1 or ENiCu-7?
ENiCu-7, by a small margin. Both rate poor for machinability — 30/100 against 20/100 for ENiCrCoMo-1; for welding the order is ENiCrCoMo-1 first (excellent, 85/100) then ENiCu-7 (very good, 72/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in ENiCrCoMo-1 and ENiCu-7 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.