Nickel Alloy CW-6MC vs CZ-100
Nickel Alloy · grade comparison
Nickel Alloy CW-6MC and CZ-100 are both nickel alloy grades. CW-6MC is the stronger of the two: yield strength 315 MPa (45.7 ksi) against 160 MPa (23.2 ksi) for CZ-100, about 97% more; tensile strength follows at 550 MPa (79.8 ksi) vs 380 MPa (55.1 ksi). CW-6MC is the more ductile: elongation 40% versus 25% for CZ-100, and CW-6MC is harder (180 HB vs 110 HB). CW-6MC is lighter (8.44 g/cm³ vs 8.85 g/cm³ for CZ-100) and CW-6MC is stiffer (200 GPa vs 180 GPa). On the shop floor, CZ-100 machines more easily (fair vs poor) and CW-6MC welds better (excellent vs good).
CW-6MCChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
CZ-100Choose it when the part is machined in volume.
CW-6MC vs CZ-100: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Compressive Strength
Hardness, Vickers
Same in both: Poisson's Ratio 0.31
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Same in both: Castability 65 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Water
Same in both: Embodied Carbon (primary production) 13 kg CO₂/kg · Typical Recycled Content 40%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | CW-6MC | CZ-100 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 3 finishes: Gold Plating, Plasma Spray, Silver Plating.
CW-6MC vs CZ-100 — frequently asked
Is CW-6MC stronger than CZ-100?
Yes. CW-6MC has a typical yield strength of 315 MPa (45.7 ksi) against 160 MPa (23.2 ksi) for CZ-100 — about 97% more. Tensile strength is 550 MPa (79.8 ksi) vs 380 MPa (55.1 ksi).
Which is cheaper, CW-6MC or CZ-100?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, CW-6MC or CZ-100?
CZ-100. Its machinability rates fair (35/100) against poor (22/100) for CW-6MC; for welding the order is CW-6MC first (excellent, 85/100) then CZ-100 (good, 60/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in CW-6MC and CZ-100 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.